中国激光, 2021, 48 (6): 0602201, 网络出版: 2021-03-09   

纳秒激光诱导超疏水硅橡胶表面微结构的分形特性 下载: 894次

Fractal Characteristics of Microstructures on a Superhydrophobic Silicone Rubber Surface Induced by a Nanosecond Laser
作者单位
1 湖北工业大学机械工程学院, 湖北 武汉 430068
2 湖北工业大学材料与化学工程学院, 湖北 武汉 430068
摘要
针对纳秒激光刻蚀硅橡胶表面产生的浸润性变化现象,采用分形理论对其表面微结构的形成及浸润性的转变过程进行了研究。当输入的激光能量密度较低时,硅橡胶表面发生局部的热解,生成了具有高自相似性的大小颗粒复合状态的粗糙结构,其表面的分形维数提升而疏水性能略有增加。随着激光能量密度增加,硅橡胶上的大颗粒进一步热解至微纳米尺度的小颗粒,其表面分形维数降低,此时液滴只与表面的微纳小颗粒凸面相接触,由此形成了超疏水表面;随着激光能量密度进一步提高,累积的热效应使表面形成了板状结构和沟壑,导致其粗糙度的增大。当激光能量的输入与硅橡胶表面热解达到平衡时,其表面的粗糙结构和分形特征不再发生明显变化,由此形成了具有较高自相似性的稳定超疏水表面。研究结果对于快速制备超疏水硅橡胶表面及调控其表面微结构具有良好的指导意义。
Abstract

Objective Silicone rubber has been widely used in aerospace and power transportation because it has stable and reliable physical properties. However, the hydrophobicity of its surface should be improved to enhance its stability in practical applications. This property can be improved more quickly and effectively by laser etching than by surface coating, plasma processing, imprinting, and other methods. Various surface microstructures can also be obtained through laser etching. The main factor that causes the change in hydrophobicity is the rough microstructure on silicone rubber surfaces after laser irradiation. However, the specific influence of its surface morphology on hydrophobicity has not yet been confirmed. Fractal dimension is a measure to characterize the irregularity of complex shapes, which can indicate the effectiveness of the space occupied by complex shapes, and has been widely used in studies on the physical properties of rough surfaces. Therefore, in this study, fractal theory and fractal dimension are introduced to explore the rough structure and geometric characteristics of silicone rubber surfaces after laser etching, establish their association with surface hydrophobicity, and provide a method for explaining the change in the wettability of rough surfaces.

Methods A silicone rubber surface was etched with an SPI nanosecond fiber laser at a maximum power of 70 W and a wavelength of 1064 nm. Silicone rubber surfaces in different wetting states were obtained by modifying the laser fluence. The wettability of the surfaces was characterized by measuring their contact and rolling angles. Fourier transform attenuated total reflection infrared spectroscopy(ART-FTIR) and energy dispersive spectromete(EDS) were then conducted to detect the chemical elements and groups on the sample surfaces, and the influence of chemical factors on surface wettability was excluded. After the rough surface microstructure was determined as the main cause of the change in wettability, the contour curves of the sample surfaces collected with a white light interferometer (BRUKE, ContourGT-K0) were drawn to calculate the fractal dimension. Combined with the scanning electron microscope(SEM) micrograph of the sample surfaces, fractal theory was introduced to analyze the micro-nanocomposite structures produced on the laser-etched silicone rubber surface.

Results and Discussions Laser treatment could significantly improve the hydrophobicity of the silicone rubber surface. The surface of the untreated silicone rubber exhibited a weak hydrophobicity with contact and rolling angles of ~110° and >90°, respectively. As the laser energy input increased, the contact angle of the silicone rubber surface increased rapidly. When the laser fluence increased to 10 J/cm 2, the contact angle increased to ~160°, whereas the rolling angle decreased to ~3°. ART-FTIR and EDS revealed that the input laser energy did not induce the changes in the chemical elements and groups on the silicone rubber surfaces. The surface wettability of the laser-treated silicone rubber was mainly determined by its three-dimensional microstructure. The silicone rubber surface was pyrolyzed locally when the laser fluence was low. Consequently, a coarse structure with a high self-similarity and a composite state of large and small particles formed, thereby improving the fractal dimension of the surface and slightly increasing the surface hydrophobicity. As the laser fluence increased, the large particles on the silicone rubber were pyrolyzed to the micro-nanoparticles, which reduced the fractal dimension of the silicone rubber surface. Droplets were only in contact with the convex surface of the small particles on the surface, creating a superhydrophobic surface. As the laser fluence further increased, a plate-like structure with trenches was produced because of thermal effects, and the roughness of the processed surface increased. When the balance between the inputted laser energy and the surface pyrolysis of silicone rubber was reached, the rough structure of the surface no longer changed significantly. As a result, a stable superhydrophobic surface with a high self-similarity was created.

Conclusions When silicon rubber is etched with a nanosecond laser, the chemical element composition and groups on the surface do not vary significantly, and wettability changes mainly because of the surface microstructure. Therefore, the fractal characteristics of the rough structure of the laser-treated silicone rubber surface are analyzed to establish the relationship between surface microstructure characteristics and hydrophobicity. As the laser fluence increases, the highest fractal dimension of 1.65 is obtained when the silicone rubber surface is irradiated with a laser fluence of 7.5 J/cm 2. A micro-nanocomposite structure with a high self-similarity simultaneously appears on the surface of the silicone rubber, thereby improving its hydrophobic properties. When the laser fluence further increases to 10 J/cm 2, the large particles on the silicone rubber surface become refined into small particles and disperse on the surface. Consequently, the surface roughness of the silicone rubber and the fractal dimension decrease to 4--5 μm and 1.40, respectively. As a result, the contact state between the silicone rubber surface and the water droplets transforms from a Wenzel model to a Cassie model. In other words, the processed surface changes from a hydrophobic state to a superhydrophobic state. When the laser energy fluence further increases, the fractal dimension increases again and stabilizes at about 1.55. When the silicone rubber is irradiated with larger laser energy, small micro-nano particles continue to be generated on the surface. These small micro-nano particles are continuously stacked on the basis of the original particles, thereby forming a composite structure with a high self-similarity again. However, when the balance between the rate of the thermal cracking of the large particles and the formation of the small micro-nano particles is obtained, the self-similarity of the surface micro-nano structure no longer changes, and the surface hydrophobicity remains stable. Therefore, the analysis of the fractal characteristics of the micro-nano structure on the silicone rubber surface after laser etching helps establish the relationship between surface structure and hydrophobicity. It also provides a basis for rapidly preparing superhydrophobic silicone rubber surfaces and regulating their surface microstructure.

陈列, 文关棋, 郭飞, 胡涛, 刘顿. 纳秒激光诱导超疏水硅橡胶表面微结构的分形特性[J]. 中国激光, 2021, 48(6): 0602201. Lie Chen, Guanqi Wen, Fei Guo, Tao Hu, Dun Liu. Fractal Characteristics of Microstructures on a Superhydrophobic Silicone Rubber Surface Induced by a Nanosecond Laser[J]. Chinese Journal of Lasers, 2021, 48(6): 0602201.

本文已被 3 篇论文引用
被引统计数据来源于中国光学期刊网
引用该论文: TXT   |   EndNote

相关论文

加载中...

关于本站 Cookie 的使用提示

中国光学期刊网使用基于 cookie 的技术来更好地为您提供各项服务,点击此处了解我们的隐私策略。 如您需继续使用本网站,请您授权我们使用本地 cookie 来保存部分信息。
全站搜索
您最值得信赖的光电行业旗舰网络服务平台!