Yb3+:Y2O3透明陶瓷激光器获得5 W连续激光输出

5 W CW Output Yb3+:Y2O3 Transparent Ceramic Laser

  • 摘要
  • 论文信息
  • 参考文献
  • 被引情况
  • PDF全文
分享:

摘要

用带尾纤输出的激光二极管作为抽运源,采用端面抽运10% Yb3+∶Y2O3多晶透明陶瓷的方式获得了连续激光输出。抽运阈值功率为5.6 W,当陶瓷介质吸收的抽运功率为31.11 W时,Yb3+∶Y2O3多晶透明陶瓷获得了最大连续激光输出功率5.48W,光光转换效率为17.6%,斜率效率为25%。同时在激光实验过程中,没有发现饱和现象,因此采用更高功率的激光二极管作为抽运源,陶瓷的激光输出功率会得到进一步提高。这一研究成果表明,多晶透明陶瓷是一种非常有潜力的激光增益介质。

Abstract

CW laser output is obtained using laser diode end-pumped polycrystalline transparent 10% Yb3+∶Y2O3 ceramic. The pump threshold is 5.6 W, the maximum output power of 5.48 W is obtained with the absorbed pump power 31.11 W, and the slope efficiency is as high as 25%. At the same time there is no saturation in laser experiment, so the higher power output of Yb3+∶Y2O3 ceramic can be obtained with laser diode of higher power. Therefore Yb3+∶Y2O3 ceramic is a potential laser material.

Newport宣传-MKS新实验室计划
补充资料

中图分类号:TN244

所属栏目:简讯

收稿日期:2003-12-23

修改稿日期:--

网络出版日期:--

作者单位    点击查看

楼祺洪:中国科学院上海光学精密机械研究所, 上海 201800
马海霞:中国科学院上海光学精密机械研究所, 上海 201800
漆云凤:中国科学院上海光学精密机械研究所, 上海 201800
董景星:中国科学院上海光学精密机械研究所, 上海 201800
魏运荣:中国科学院上海光学精密机械研究所, 上海 201800

【1】Yanagitani T, Yagi H, Ichikawa M. Manufacture method of fine powder of YAG. Japan Patent, 1998, 10-101333

【2】Yanagitani T, Yagi H, Hiro Y. Manufacture method of fine powder of YAG. Japan Patent, 1998, 10-101411

【3】Lu J, Song J, Prabhu M et al.. High-power Nd∶Y3Al5O12 ceramic laser. Jpn. J. Appl. Phys., 2000, 39:1048~1050

【4】Kong J, Tang D Y, Shen D Y et al.. Diode pumped Yb∶Y2O3 ceramic laser. Proc. SPIE, 2002, 4914:69~76

【5】Lu J, Bission J F, Takaichi K et al.. Yb3+∶Sc2O3 ceramic laser. Appl. Phys. Lett., 2003, 83(6):1101~1103

【6】Lu J, Takaichi K, Uematsu T et al.. Promising ceramic laser material: Highly transparent Nd3+∶Lu2O3 ceramic. Appl. Phys. Lett., 2002, 81(23):4324~432

您的浏览器不支持PDF插件,请使用最新的(Chrome/Fire Fox等)浏览器.或者您还可以点击此处下载该论文PDF