TiO2晶型及其相变的高温拉曼光谱研究

High Temperature Raman Spectroscopic Study of Titania and Its Phase Transformation
作者单位
1 上海大学,上海市钢铁冶金新技术开发应用重点实验室,上海,200072
2 上海大学,化学和化学工程系,上海,200072
3 上海大学,材料科学和材料工程学院,上海,200072
摘要
本文测量了锐钛矿型和金红石型TiO2常温至1923K的高温拉曼光谱,观察了锐钛矿型TiO2在1373K~1473K间发生相变,不可逆转化为金红石型TiO2,分析了特征峰随温度变化的规律以及两种结构相的温度依赖性.并为不同晶型TiO2的研究、生产和应用提供重要的实验依据.
Abstract
Raman spectra of anatase and rutile crystal phases of titania at ambient and high temperatures up to 1923 K were measured. Phase transition from anatase to rutile phase at temperature range of 1373~1473 K was observed. Temperature dependence of the characteristics of their Raman peaks was analysised. It offers experimental basis for research, manufacturing and applications of various crystal types of titania.

尤静林, 蒋国昌, 王桢枢, 潘晓燕, 马学鸣. TiO2晶型及其相变的高温拉曼光谱研究[J]. 光散射学报, 2004, 16(2): 95. 尤静林, 蒋国昌, 王桢枢, 潘晓燕, 马学鸣. High Temperature Raman Spectroscopic Study of Titania and Its Phase Transformation[J]. The Journal of Light Scattering, 2004, 16(2): 95.

本文已被 5 篇论文引用
被引统计数据来源于中国光学期刊网
引用该论文: TXT   |   EndNote

相关论文

加载中...

关于本站 Cookie 的使用提示

中国光学期刊网使用基于 cookie 的技术来更好地为您提供各项服务,点击此处了解我们的隐私策略。 如您需继续使用本网站,请您授权我们使用本地 cookie 来保存部分信息。
全站搜索
您最值得信赖的光电行业旗舰网络服务平台!