红外与激光工程, 2001, 30 (5): 357, 网络出版: 2006-04-28
2m长As-Se-Te玻璃红外光纤传像束
2 meter length IR coherent bundle of As-Se-Te glass fibers
As-Se-Te玻璃红外光纤 光纤损耗 传像束 填充系数K As-Se-Te IR optical fiber Fiber optic loss Coherent bundles Packing coefficient K
摘要
文中介绍了传输2~12μmAs-Se-Te玻璃红外光纤所用原料提纯和玻璃熔制工艺改进的方法.分析了损耗、填充系数K和面反射对透过率的影响.将制备出的红外玻璃光纤,用WQF-400傅里叶变换红外光纤光谱仪测试其损耗,光纤损耗值明显降低.把单丝直径φ≤80μm的As-Se-Te玻璃光纤制成100像元×100像元、长度为2m的传像束.前、后两端分别配置可调焦的红外透镜,入端对准5m处400℃黑体炉φ=3mm的小孔,出端与热像仪连接,经过光学扫描和信号处理后,在计算机屏幕上显示出圆形的黑体?认?结果表明,在特殊环境中用As-Se-Te玻璃红外传像束,传输热像是最佳设计方案之一.
Abstract
In this paper, improving methods of purifying raw el ements and melting technology of As-Se-Te glass fibers in 2~12μm wave band w ere introduced. Effect of the fiber loss, packing fracting K and surface ref lection on the transmittance was analyzed respectively. The loss of As-Se-Te g lass fiber measured by FTIR spectrometer was obviously lower. By using the As-S e-Te glass fibers, 100×100 pixels 2m length coherent fiber bundles were made. While coupling one end of the bundles to the target area of the IR TV camera thr ough the lens system, the other end was aimed at a 3mm diameter hole at 5m away. This small hole had been homogeneously injected by ideal radiator. The thermal image was delivered through the boundles and was clearly observed on the TV scre en. The results show that As-Se-Te IR coherent bundles are one of the best des ign for delivery of thermal images in special circumstances
吕步云, 杨克武, 薛洪逵, 闫晋力, 张杏梅, 费锦东, 刘纯胜. 2m长As-Se-Te玻璃红外光纤传像束[J]. 红外与激光工程, 2001, 30(5): 357. 吕步云, 杨克武, 薛洪逵, 闫晋力, 张杏梅, 费锦东, 刘纯胜. 2 meter length IR coherent bundle of As-Se-Te glass fibers[J]. Infrared and Laser Engineering, 2001, 30(5): 357.