Chinese Optics Letters, 2004, 2 (4): 04229, Published Online: Jun. 6, 2006  

Spectroscopic properties of Er^(3+)-doped AlF_(3)-La_(2)O_(3)-Al_(2)O_(3)-SiO_(2) glasses

Author Affiliations
Shanghai Institute of Optics and Fine Mechanics, Chinese Academy of Sciences, Shanghai 201800
Abstract
Er^(3+)-doped fluoride lanthanum aluminosilicate glasses with compositions of (65-x/2)SiO_(2).(25-x/2)Al_(2)O_(3).xAlF_(3).9.1La_(2)O_(3).0.6Er_(2)O_(3).0.3Yb_(2)O_(3) (x = 4, 8, 12, 20, 30) (mol%) were prepared and their glass transitiontemperatures and spectroscopic properties were investigated. The Ω_(2), Ω_(4), and Ω_(6) intensity parameters of glasses were calculated by Judd-Ofelt theory from absorption curves. It was found that glasses transition temperature and melting temperature decreased with the increase of fluoride content in glass, Ω_(2) decreased gradually with the increase of AlF_(3) content, but both Ω_(4) and Ω_(6) did not increase until AlF_(3) content increased to 30 mol%. The quantum efficiency of ^(4)I_(13/2) to ^(4)I_(15/2) transition of Er^(3+) ions increases with the increase of AlF_(3) content in glass. Fluorescent lifetime is longer in glass containing more AlF_(3) content.

Debao Zhang, Baoyu Chen, Zhuping Liu, Shunguang Li, Lili Hu. Spectroscopic properties of Er^(3+)-doped AlF_(3)-La_(2)O_(3)-Al_(2)O_(3)-SiO_(2) glasses[J]. Chinese Optics Letters, 2004, 2(4): 04229.

关于本站 Cookie 的使用提示

中国光学期刊网使用基于 cookie 的技术来更好地为您提供各项服务,点击此处了解我们的隐私策略。 如您需继续使用本网站,请您授权我们使用本地 cookie 来保存部分信息。
全站搜索
您最值得信赖的光电行业旗舰网络服务平台!