光学学报, 2006, 26 (10): 1585, 网络出版: 2006-10-31   

常压化学气相沉积技术生长ZnO∶H薄膜的光学性质

Optical Properties of ZnO∶H Films Grown by Atmospheric Pressure Metal Organic Chemical Vapor Deposition (APMOCVD)
作者单位
南昌大学教育部发光材料与器件工程研究中心, 南昌 330047
摘要
采用常压金属有机物化学气相沉积技术(APMOCVD),以二乙基锌(DEZn)为Zn源,去离子水(H2O)为氧源,N2作载气,在外延ZnO薄膜的反应气氛中通入少量氢气,在cAl2O3衬底上生长出了ZnO∶H薄膜。用X射线双晶衍射和光致发光谱对ZnO∶H薄膜的结晶性能和光学性质进行表征。结果表明,ZnO∶H薄膜(002)和(102)面的Ω扫描半峰全宽分别为46.1 mrad和81.4 mrad,表明该薄膜具有良好的结晶性能;室温下,ZnO∶H薄膜具有较强的紫外光发射(380 nm),在低温10 K光致发光谱中观测到位于3.3630 eV处与氢相关的中性施主束缚激子峰(I4)及其位于3.331 eV处的双电子卫星峰(TES)。采用退火的方法,通过观测I4峰的强度变化,研究了氢在ZnO∶H薄膜中的热稳定性。发现随着退火温度的升高,I4峰的强度逐渐减弱,表明在高温下退火,氢会从ZnO薄膜中逸出。
Abstract
ZnO∶H thin films were prepared on cAl2O3 substrate by adding a little of H2 gas in the reaction gas when depositing ZnO films using atmospheric pressure metal organic chemical vapor deposition (APMOCVD) with carrier gas of nitrogen. Zn(C2H5)2 (DEZn) and H2O were used as Zn and O precursors, respectively. The crystallizing performance and optical properties were studied with doublecrystal Xray diffraction and photoluminescence. The full widths at half maximum of the (002) and (102) omega rocking curves of ZnO∶H films were 46.1 mrad and 81.4 mrad, respectively, indicating the high crystal quality of the films. The room temperature photoluminescence (PL) spectra showed that there was a strong ultraviolet emission at 380 nm. Meanwhile, a strong hydrogen-related bound exciton peak (I4) at 3.363 eV and its two electron satellite at 3.331 eV were observed in the low temperature PL spectra at 10 K. In addition, the thermal stability of hydrogen in ZnO∶H films were investigated by observing the intensity change of I4 peak during the annealing process. The results showed that the intensity of I4 peak decreased with the annealing temperature increasing, indicating the hydrogen would evolve out from ZnO∶H films annealed at high temperature.

李璠, 王立, 戴江南, 蒲勇, 方文卿, 江风益. 常压化学气相沉积技术生长ZnO∶H薄膜的光学性质[J]. 光学学报, 2006, 26(10): 1585. 李璠, 王立, 戴江南, 蒲勇, 方文卿, 江风益. Optical Properties of ZnO∶H Films Grown by Atmospheric Pressure Metal Organic Chemical Vapor Deposition (APMOCVD)[J]. Acta Optica Sinica, 2006, 26(10): 1585.

本文已被 1 篇论文引用
被引统计数据来源于中国光学期刊网
引用该论文: TXT   |   EndNote

相关论文

加载中...

关于本站 Cookie 的使用提示

中国光学期刊网使用基于 cookie 的技术来更好地为您提供各项服务,点击此处了解我们的隐私策略。 如您需继续使用本网站,请您授权我们使用本地 cookie 来保存部分信息。
全站搜索
您最值得信赖的光电行业旗舰网络服务平台!