高强镀锌钢激光填粉焊接工艺试验研究

Process study on laser welding of high strength galvanized steel with powder filling
作者单位
1 湖南大学 汽车车身先进设计制造国家重点实验室 长沙 410082
2 中国航空工业集团公司 成都飞机工业(集团)有限责任公司,成都 610092
摘要
为了研究高强镀锌钢激光填粉焊接工艺,采用正交实验法优化了激光功率、焊接速度、离焦量等焊接工艺参量。结果表明,激光填粉焊接速率过低时,焊缝易于产生熔质堆积和焊接孔洞; 增大离焦量可实现粉末的有效利用; 装配间隙为0.25mm(母材厚度的31%)时,高强镀锌钢激光填粉焊接的最佳工艺参量为激光功率1500W,焊接速率30mm/s,离焦量12mm,此时,焊缝表面成形良好,其拉伸试验断裂产生在母材。
Abstract
In order to optimize the process parameters in laser welding of high-strength galvanized steel with powder filling, orthogonal experimental tests were used to analyze such process parameters as laser power, welding speed and the defocusing distance. The test results show that the accumulation of the molten mass and the welding holes might occur at low welding speed; the defocusing distance should be increased to achieve the effective addition of the powder. The optimization process parameters for laser welding of high-strength galvanized steel with powder filling were 1500W laser power, 30mm/s welding speed and 12mm defocusing distance. Under these welding conditions, good weld performance was obtained and the base material was broken in tensile fracture tests.

徐磊, 刘西霞, 李庆福, 胡光蓉, 张屹. 高强镀锌钢激光填粉焊接工艺试验研究[J]. 激光技术, 2014, 38(1): 1. XU Lei, LIU Xixia, LI Qingfu, HU Guangrong, ZHANG Yi. Process study on laser welding of high strength galvanized steel with powder filling[J]. Laser Technology, 2014, 38(1): 1.

本文已被 3 篇论文引用
被引统计数据来源于中国光学期刊网
引用该论文: TXT   |   EndNote

相关论文

加载中...

关于本站 Cookie 的使用提示

中国光学期刊网使用基于 cookie 的技术来更好地为您提供各项服务,点击此处了解我们的隐私策略。 如您需继续使用本网站,请您授权我们使用本地 cookie 来保存部分信息。
全站搜索
您最值得信赖的光电行业旗舰网络服务平台!