中国激光, 2007, 34 (4): 525, 网络出版: 2007-04-25   

含偶氮苯侧链型聚酰亚胺的合成及光致变色性能

Synthesis and Research of Photochromism Based on Side-Polyimide Containing Azobenzene Group
作者单位
1 江苏大学化学化工学院, 江苏 镇江 212013
2 东南大学化学化工学院, 江苏 南京 210096
3 南京大学光通信工程研究中心, 江苏 南京 210093
摘要
用5,5′-(六氟异丙基)-二-(2-氨基苯酚)(6FHP)、均苯四甲酸酐(PMDA)及分散红1(DR1)合成了具有光致变色性能的含偶氮苯侧链型聚酰亚胺。利用红外(IR)、紫外-可见(UV-Vis)、示差扫描量热(DSC)和热失重分析(TGA)等手段对该光致变色聚合物材料进行了结构和热性能表征。示差扫描量热分析测得其玻璃化转变温度为298 ℃,热重分析测得其热分解温度为365 ℃,表明具有非常好的热稳定性。研究了该材料的N-甲基-2-吡咯烷酮(NMP)溶液和聚合物薄膜在紫外光诱导下的光异构化及热回复异构化行为。结果表明,在一定波长(365 nm)紫外光诱导下均能发生光致变色现象,对于实现偶氮材料的永久光致双折射和永久光存储具有一定意义。
Abstract
The side polyimide containing azobenzene group was synthesized with photochromism property from 2,2-Bis (3-amino-4-hydroxyyphenyl) hexafluoropropane (6FHP), pyromellitic dianhydride (PMDA) and dispersed red 1 (DR1). The chemical structure and thermal properties of polyimide were characterized using Fourier transform infrared (FT-IR), ultraviolet-visible (UV-Vis) spectroscopy, differential scanning calorimeter (DSC), and thermal gravimetric analysis (TGA). The DSC and TGA exhibited the glass transition temperature (Tg) and the decomposition temperature (Td) of polymer were 298 ℃ and 365 ℃, respectively. These results showed that the material had excellent thermal stability. The UV-induced trans/ cis photoisomerization and the thermal reflex-isomerization behavior were investigated for the polymer in solution and in film. The results indicate that the polymer solution and polymer film can undergo photochromism after a given UV wavelength (365 nm) photoinduction. This showed that the polyimide could be used to carry out perpetuity photoinduced birefringence and recording.

邱凤仙, 徐红良, 杨冬亚, 胡凡明, 周钰明, 刘举正, 张旭苹. 含偶氮苯侧链型聚酰亚胺的合成及光致变色性能[J]. 中国激光, 2007, 34(4): 525. 邱凤仙, 徐红良, 杨冬亚, 胡凡明, 周钰明, 刘举正, 张旭苹. Synthesis and Research of Photochromism Based on Side-Polyimide Containing Azobenzene Group[J]. Chinese Journal of Lasers, 2007, 34(4): 525.

本文已被 6 篇论文引用
被引统计数据来源于中国光学期刊网
引用该论文: TXT   |   EndNote

相关论文

加载中...

关于本站 Cookie 的使用提示

中国光学期刊网使用基于 cookie 的技术来更好地为您提供各项服务,点击此处了解我们的隐私策略。 如您需继续使用本网站,请您授权我们使用本地 cookie 来保存部分信息。
全站搜索
您最值得信赖的光电行业旗舰网络服务平台!