光学学报, 1992, 12 (8): 723, 网络出版: 2007-09-11   

LB薄膜中四新戊氧基酞菁锌和四壬基酞菁铜分子聚集体的吸收光谱的温度特性

Temperature dependence of absorption spectra of aggregates in the LB films of tetra-neopentoxy phthalocyanine zine and tetra-nonyl phthalocyanine copper
作者单位
中国科学院上海光学精密机械研究所, 上海 201800
摘要
本文制备了四新戊氧基酞菁锌(Tetra-neopentoxy phthalocyanine zine)(TNPPeZn)和四壬基酞菁铜(Tetra-nonyl phthalocyanine copper)(TNPeCu)两种酞菁衍生物的Langmuir-Blodgett(LB)薄膜.通过测量10~473K温度下的吸收光谱,研究了两种薄膜的分子聚集状态.TNPPeZn的LB薄膜中,存在着分子单体和分子二聚体,在吸收光谱中分别表现为680nm和620nm的吸收峰.随着温度的升高,分子单体逐渐转变为分子二聚体,这个过程是不可逆的.TNPeCu的LB薄膜中,除了分子单体和分子二聚体以外,还有吸收为740nm的分子J聚集体存在.随着温度的变化,J聚集体发生可逆变化.
Abstract
Langmuir-Blodgett (LB) films of tetra-neopentoxy phthaloeyanine zine and tetra-nonyl phthalocyanine copper are prepared, Absorption spectra at different temperature are measured and aggregates of the films are studied. There are a strong peak at 680 nm and a sideband at 620 nm which are corresponding to monomer and dimer respectively in absorption spectra of tetra-neopentoxy phthalocyanine zine films in room temperature. The monomer is transformed irreversibly into the dimer gradually with temperature increasing. The absorption spectra of tetra-nonyl phthalocyanine copper LB films in room temperature show that there are monomer, dimer and J-aggregates which causes a strong peak at 740 nm, in the LB films. The J-aggregates is destroyed at high temperature and restored again when the temperature decreased.

罗涛, 张伟清, 祁长鸿, 干福熹. LB薄膜中四新戊氧基酞菁锌和四壬基酞菁铜分子聚集体的吸收光谱的温度特性[J]. 光学学报, 1992, 12(8): 723. 罗涛, 张伟清, 祁长鸿, 干福熹. Temperature dependence of absorption spectra of aggregates in the LB films of tetra-neopentoxy phthalocyanine zine and tetra-nonyl phthalocyanine copper[J]. Acta Optica Sinica, 1992, 12(8): 723.

本文已被 3 篇论文引用
被引统计数据来源于中国光学期刊网
引用该论文: TXT   |   EndNote

相关论文

加载中...

关于本站 Cookie 的使用提示

中国光学期刊网使用基于 cookie 的技术来更好地为您提供各项服务,点击此处了解我们的隐私策略。 如您需继续使用本网站,请您授权我们使用本地 cookie 来保存部分信息。
全站搜索
您最值得信赖的光电行业旗舰网络服务平台!