中国激光, 2014, 41 (8): 0803005, 网络出版: 2014-07-15
激光焊接不等厚异种钢接头组织与性能研究
Microstructure and Mechanical Properties of Laser Welded Joints for Dissimilar Steel with Different Thicknesses
激光光学 激光拼焊 异种钢 显微组织 力学性能 laser optics laser tailor-welded dissimilar steel microstructure mechanical property
摘要
针对汽车用钢的焊接问题,利用光学显微镜、扫描电镜、硬度和拉伸试验研究分析了不等厚异种钢激光拼焊板接头的组织及性能。结果表明,焊缝区为板条马氏体组织,板条之间有残留奥氏体组织存在。熔合区附近的组织结构比较复杂,主要由马氏体和贝氏体构成。而相变诱发塑性(TRIP)钢热影响区组织主要由贝氏体和铁素体组成,且晶粒比较细小,双相钢(DP)接头热影响区中存在显著的马氏体组织,但几乎不存在过热区组织。接头焊缝区的硬度达到母材的1.6倍以上,此外接头宏观断裂发生在薄板DP钢的母材区。
Abstract
Aiming at the welding problem of steel used in automobile, the microstructure and property of joints in laser welded tailored sheets for dissimilar steel with different thicknesses are analyzed by optical microscope (OM), scanning electron microscope (SEM), hardness and tensile test. The results indicate that weld zone are lath martensite, and the laths mixed with retained austenite. Microstructure near the fusion line is more complex, mainly consists of martensite and bainite. Heat affected zone (HAZ) of transformation induced plasticity (TRIP) steel is mainly composed of bainite and ferrite, and the grains are relatively small. There are significant martensite existed in HAZ of dual phase (DP) steel, and the overheated zone is almost non-existent. The hardness in weld zone is more than 1.6 times as the parent metal. Macroscopic fracture of joint occurs in base metal of thinner DP steel sheet.
景财年, 范吉超, 倪晓梅, 李怀学, 刘鹏, 张宜生. 激光焊接不等厚异种钢接头组织与性能研究[J]. 中国激光, 2014, 41(8): 0803005. Jing Cainian, Fan Jichao, Ni Xiaomei, Li Huaixue, Liu Peng, Zhang Yisheng. Microstructure and Mechanical Properties of Laser Welded Joints for Dissimilar Steel with Different Thicknesses[J]. Chinese Journal of Lasers, 2014, 41(8): 0803005.