激光熔覆制备SiC/Ni基复合涂层及其耐冲蚀性能

Synthesis of SiC/Ni Composite Coatings by Laser Cladding and Property of Erosion Resistance
作者单位
浙江工业大学材料表面工程研究所, 机械制造及自动化教育部重点实验室, 浙江 杭州 310014
摘要
采用激光熔覆技术在45#钢表面分别制备了Ni60A涂层及SiC/Ni60A复合涂层。采用光学显微镜(OM)、扫描电镜(SEM)和X射线衍射(XRD)仪对涂层进行了显微组织和物相分析, 并测试了熔覆层的显微硬度和耐冲蚀磨损性能。结果表明, 在激光作用下, SiC由于具有较小的生成热容易溶解在合金涂层中。熔覆层的物相主要由γ(Ni-Cr-Fe)固溶体及Fe7C3 , Fe0.79C0.12Si0.09等化合物组成。在固溶强化、第二相强化及细晶强化的共同作用下, SiC/Ni60A涂层的抗冲蚀性能显著提高, 涂层的显微硬度也明显增加。
Abstract
Ni60A and SiC/Ni60A coatings had been synthesized by laser cladding on 45# steel substrate. Optical microscopy (OM), scanning electron microscopy (SEM) and X-ray diffraction (XRD) were used to analyse the microstructure and metallographic. The microhardness and erosion resistance performance had also been investigated. Results reveal that SiC can easily be dissolved in alloy coatings due to its low heat of formation. The phase of coatings is mainly composed of γ(Ni-Cr-Fe) solid solution, Fe7C3 and Fe0.79C0.12Si0.09. As the coaction of solution strengthening, second-phase strengthening and fine-crystal strengthening, the erosion performance of SiC/Ni60A composite coatings has been significantly increased and the microhardness has also been evidently raised.

徐斌, 楼白杨, 白万金, 董刚. 激光熔覆制备SiC/Ni基复合涂层及其耐冲蚀性能[J]. 中国激光, 2008, 35(1): 147. Xu Bin, Lou Baiyang, Bai Wanjin, Dong Gang. Synthesis of SiC/Ni Composite Coatings by Laser Cladding and Property of Erosion Resistance[J]. Chinese Journal of Lasers, 2008, 35(1): 147.

本文已被 7 篇论文引用
被引统计数据来源于中国光学期刊网
引用该论文: TXT   |   EndNote

相关论文

加载中...

关于本站 Cookie 的使用提示

中国光学期刊网使用基于 cookie 的技术来更好地为您提供各项服务,点击此处了解我们的隐私策略。 如您需继续使用本网站,请您授权我们使用本地 cookie 来保存部分信息。
全站搜索
您最值得信赖的光电行业旗舰网络服务平台!