中国激光, 2008, 35 (8): 1161, 网络出版: 2008-08-16   

飞秒激光在LiNbO3晶体上烧蚀衍射光栅

Diffraction Gratings Ablated on LiNbO3 Crystal by Femtosecond Laser Pulses
作者单位
1 信阳师范学院物理电子工程学院, 河南 信阳 464000
2 华中科技大学光电子科学与工程学院武汉光电国家实验室, 湖北 武汉 430074
摘要
利用脉冲宽度为50 fs,中心波长为800 nm,重复频率为1000 Hz的飞秒激光脉冲在LiNbO3晶体上烧蚀表面衍射光栅,采用632.8 nm的He-Ne激光测量不同光栅的衍射效率。在激光脉冲能量和光栅常数相同的情况下,烧蚀速率由20 μm/s增大到200 μm/s时,所加工光栅的1级衍射效率从1.7%增大到2.3%; 如果光栅常数和烧蚀速率不变,将激光脉冲能量由70 nJ增大到110 nJ,所加工光栅的1级衍射效率从1.9%减小到1.3%; 随着光栅常数的增大,在LiNbO3晶体上烧蚀光栅的各级衍射效率也随之增加。对实验结果进行理论分析表明,可以通过提高烧蚀速率、降低激光脉冲能量和增大光栅常数来提高飞秒激光加工光栅的衍射效率。
Abstract
Surface diffraction gratings are written on LiNbO3 crystal by femtosecond laser pulses with the wavelength of 800 nm, pulse duration of 50 fs and repetition frequency of 1000 Hz. The diffraction efficiencies of the gratings ablated with various parameters are measured by He-Ne laser with the wavelength of 632.8 nm. The 1-order diffraction efficiencies of the gratings improve from 1.7% to 2.3% with the increase of ablation speed from 20 μm/s to 200 μm/s, and decrease from 1.9% to 1.3% with the increase of pulse energy from 70 nJ to 110 nJ, respectively. The experimental and theoretical results show that the diffraction efficiencies of gratings can be improved by increasing ablation speed and grating constant or decreasing pulse energy.

余本海, 李玉华, 戴能利, 郑启光, 陆培祥. 飞秒激光在LiNbO3晶体上烧蚀衍射光栅[J]. 中国激光, 2008, 35(8): 1161. Yu Benhai, Li Yuhua, Dai Nengli, Zheng Qiguang, Lu Peixiang. Diffraction Gratings Ablated on LiNbO3 Crystal by Femtosecond Laser Pulses[J]. Chinese Journal of Lasers, 2008, 35(8): 1161.

本文已被 2 篇论文引用
被引统计数据来源于中国光学期刊网
引用该论文: TXT   |   EndNote

相关论文

加载中...

关于本站 Cookie 的使用提示

中国光学期刊网使用基于 cookie 的技术来更好地为您提供各项服务,点击此处了解我们的隐私策略。 如您需继续使用本网站,请您授权我们使用本地 cookie 来保存部分信息。
全站搜索
您最值得信赖的光电行业旗舰网络服务平台!