钛合金稀释作用对NiCrBSiC激光熔覆层微观结构的影响

Influence of Ti Substrate Dilution on the Microstructure of NiCrBSiC Laser Clad Coatings
作者单位
1 天津工业大学机械电子学院, 天津 300160
2 天津市现代机电装备技术重点实验室, 天津 300160
3 天津钢管集团股份有限公司, 天津 300301
摘要
采用横流CO2激光器在TC4合金表面熔覆NiCrBSiC合金涂层,探讨了激光熔覆工艺参数对涂层稀释率和微观结构的影响。结果表明,在激光功率密度和辐照时间相同的条件下,大直径(D=6 mm)光斑热源能获得更深的基体熔化深度,涂层的稀释率较高,涂层中的强化相主要为TiB2和TiC相; 小直径(D=3 mm)光斑热源基体熔化深度较浅,涂层的稀释率较低,涂层中的强化相为CrB以及少量的M23(CB)6和TiC相。
Abstract
NiCrBSiC laser clad coatings are fabricated on TC4 substrate using CW-CO2 laser. The influence of processing parameter on the microstructure and dilution rate of the coatings is examined. Under the same power density and irradiation time, the depth of substrate fusion is deeper, the dilution rate of the coatings is higher and the reinforcing phases are mainly TiB2 and TiC when the laser beam diameter is lager (D=6 mm). The depth of substrate fusion is shallower, the dilution rate of the coatings is lower and the reinforcing phases are mainly CrB and small amount of M23(CB)6 and TiC when the laser beam diameter is smaller (D=3 mm).

孙荣禄, 刘智勇, 牛伟, 雷贻文. 钛合金稀释作用对NiCrBSiC激光熔覆层微观结构的影响[J]. 中国激光, 2008, 35(11): 1741. Sun Ronglu, Liu Zhiyong, Niu Wei, Lei Yiwen. Influence of Ti Substrate Dilution on the Microstructure of NiCrBSiC Laser Clad Coatings[J]. Chinese Journal of Lasers, 2008, 35(11): 1741.

本文已被 3 篇论文引用
被引统计数据来源于中国光学期刊网
引用该论文: TXT   |   EndNote

相关论文

加载中...

关于本站 Cookie 的使用提示

中国光学期刊网使用基于 cookie 的技术来更好地为您提供各项服务,点击此处了解我们的隐私策略。 如您需继续使用本网站,请您授权我们使用本地 cookie 来保存部分信息。
全站搜索
您最值得信赖的光电行业旗舰网络服务平台!