激光冲击处理钛合金

Laser Shock Processing of Titanium Alloy
作者单位
北京航空制造工程研究所高能束流加工技术国防科技重点实验室, 北京 100024
摘要
介绍了激光冲击处理(LSP)的特点和应用情况,研究了激光冲击处理对钛合金表面轮廓、残余应力和疲劳性能的影响。结果表明,经激光冲击处理后效果十分明显,钛合金获得光斑大小的凹坑,凹陷值10~20 μm,残余应力最大可达-600 MPa以上,表面残余应力水平与高强度喷丸相当,但塑性变形程度明显大于喷丸;合适的激光参数和搭接率可以获得光滑平整的冲击区,双光束冲击处理涡轮叶片后有明显冲击痕迹和残余压应力,并且没有发现变形和裂纹。
Abstract
The characteristic and application of laser shock processing (LSP) was introduced, then the surface profile, surface residual stress and fatigue properties of laser shock processed titanium alloy were studied. The results showed that laser shock processing had obvious effects on titanium alloy. There was shocked zone on the surface of the metal after laser shock processing, which with the same size as laser spot and depression of 10~20 μm, the most residual stress was about -600 MPa, which corresponded to the result with intense shot peening, but the intensity of plastic deformation was much more than that of shot peening. Suitable laser parameters and overlap rate can gain smooth and even surface, there were obvious marks, little deformation and no cracks on the surface of dual beam laser shock processed titanium turbine blade.

邹世坤, 曹子文, 刘方军. 激光冲击处理钛合金[J]. 中国激光, 2007, 34(s1): 4. 邹世坤, 曹子文, 刘方军. Laser Shock Processing of Titanium Alloy[J]. Chinese Journal of Lasers, 2007, 34(s1): 4.

本文已被 2 篇论文引用
被引统计数据来源于中国光学期刊网
引用该论文: TXT   |   EndNote

相关论文

加载中...

关于本站 Cookie 的使用提示

中国光学期刊网使用基于 cookie 的技术来更好地为您提供各项服务,点击此处了解我们的隐私策略。 如您需继续使用本网站,请您授权我们使用本地 cookie 来保存部分信息。
全站搜索
您最值得信赖的光电行业旗舰网络服务平台!