LiM(M=Ca, Sr, Ba)BO3∶Dy3+材料的发光特性

Luminescent Characteristics of LiM(M=Ca, Sr, Ba)BO3∶Dy3+ Phosphor
作者单位
河北大学 物理科学与技术学院, 河北 保定071002
摘要
采用固相法制备了LiM(M=Ca, Sr, Ba)BO3∶Dy3+材料,并研究了材料的发光特性。LiM(M=Ca, Sr, Ba)BO3∶Dy3+材料的发射光谱均呈多峰发射,对应于Ca,Sr,Ba,其主发射峰分别是Dy3+的4F9/2→6H15/2(484,486,486 nm),6H13/2(577,578,578 nm)和6H11/2(668,668,666 nm)跃迁。监测黄色发射峰时,所得激发光谱峰值位置相同,主激发峰分别为331,368, 397,433,462,478 nm,对应Dy3+的6H15/2→4D7/2,6P7/2,6M21/2,4G11/2,4I15/2和6F9/2跃迁。研究了敏化剂Ce3+及电荷补偿剂Li+、Na+和K+对LiM(M=Ca, Sr, Ba)BO3∶Dy3+材料发光强度的影响。结果显示:加入敏化剂Ce3+提高了材料的发光强度,发光强度最大处对应的Ce3+浓度为3%;加入电荷补偿剂Li+、Na+和K+后,材料的发光强度也得到了明显提高,但发光强度最大处对应的Li+、Na+和K+浓度不同,依次为4%、4%和3%。
Abstract
LiM(M=Ca,Sr,Ba)BO3∶Dy3+ phosphors were synthesized by solid state reaction, and their luminescet characteristics were investigated. The emission spectra of LiM(M=Ca,Sr,Ba)BO3∶Dy3+ phosphors show several bands, and the main emission peaks corresponding to Ca, Sr and Ba ion are the 4F9/2→6H15/2(484, 486 and 486 nm), 6H13/2(577, 578 and 578 nm) and 6H11/2(668, 668 and 666 nm) typical transitions of Dy3+. The excitation spectra for the yellow emission have the same excitation peaks located at 331, 368, 397, 433, 462 and 478 nm,corresponding to the 6H15/2→4D7/2, 6P7/2, 6M21/2, 4G11/2, 4I15/2 and 6F9/2 transitions of Dy3+. The effects of doping Ce3+or Li+, Na+, K+ on the luminescence intensities of LiM(M=Ca,Sr,Ba)BO3∶Dy3+ phosphors were studied, and the results showed that the intensities of LiM(M=Ca,Sr,Ba)BO3∶Dy3+ phosphors are obviously effected. The intensities increase with increasing Ce3+ concentration and reache the maximum value at 3%. Under the condition of doping Li+, Na+ and K+, the intensities are enhanced, however, the charge compensation concentration corresponding to the maximum emission intensity is different with different charge compensation ions, and the optimal concentrations are 4%, 4% and 3% corresponding to Li+, Na+ and K+, respectively.

李盼来, 杨志平, 王颖, 王志军, 郭庆林, 李旭. LiM(M=Ca, Sr, Ba)BO3∶Dy3+材料的发光特性[J]. 发光学报, 2009, 30(5): 606. LI Pan-lai, YANG Zhi-ping, WANG Ying, WANG Zhi-jun, GUO Qing-lin, LI Xu. Luminescent Characteristics of LiM(M=Ca, Sr, Ba)BO3∶Dy3+ Phosphor[J]. Chinese Journal of Luminescence, 2009, 30(5): 606.

本文已被 2 篇论文引用
被引统计数据来源于中国光学期刊网
引用该论文: TXT   |   EndNote

相关论文

加载中...

关于本站 Cookie 的使用提示

中国光学期刊网使用基于 cookie 的技术来更好地为您提供各项服务,点击此处了解我们的隐私策略。 如您需继续使用本网站,请您授权我们使用本地 cookie 来保存部分信息。
全站搜索
您最值得信赖的光电行业旗舰网络服务平台!