Er3+/Tm3+/Yb3+ tridoped oxyfluoride glass ceramics with efficient upconversion white-light emission Download: 636次

Author Affiliations
1 School of Optical-Electrical and Computer Engineering, University of Shanghai for Science and Technology, Shanghai 200093, China
2 College of Optical and Electronic Technology, China Jiliang University, Hangzhou 310018, China
Abstract
A novel Tm<sup><sup>3+</sup></sup>/Er<sup><sup>3+</sup></sup>/Yb<sup><sup>3+</sup></sup> triply-doped glass ceramics containing BaF2 nano-crystals are successfully prepared. Fluoride nanocrystals BaF2 are successfully precipitated in glass matrix, which is affirmed by the X-ray diffraction results. The intense blue (476 nm), green (543 nm), and red (656 nm) emissions of the glass ceramics are simultaneously observed at room temperature under 980-nm excitation, and the emission luminescence intensity increases signiˉcantly compared with the precursor glass, which is attributed to the low phonon energy of °uoride nanocrystals when rare-earth ions are incorporated into the precipitated BaF2 nanocrystals. Under 980-nm excitation at 400 mW, the international commission on illumination (CIE) chromaticity coordinate (X = 0.278, Y = 0.358) of the tridoped oxy°uoride glass ceramics' upconversion emissions is close to the standard white-light illumination (X = 0.333, Y = 0.333). The results indicate that Tm<sup><sup>3+</sup></sup>/Er<sup><sup>3+</sup></sup>/Yb<sup><sup>3+</sup></sup> triply doped glass ceramics can act as suitable materials for potential three-dimensional displays applications.

Chenxia Li, Shiqing Xu, Renguang Ye, Shilong Zhao, Degang Deng, Songlin Zhuang. Er3+/Tm3+/Yb3+ tridoped oxyfluoride glass ceramics with efficient upconversion white-light emission[J]. Chinese Optics Letters, 2010, 8(1): 66.

关于本站 Cookie 的使用提示

中国光学期刊网使用基于 cookie 的技术来更好地为您提供各项服务,点击此处了解我们的隐私策略。 如您需继续使用本网站,请您授权我们使用本地 cookie 来保存部分信息。
全站搜索
您最值得信赖的光电行业旗舰网络服务平台!