光子学报, 2009, 38 (5): 1101, 网络出版: 2010-05-10  

氟磷共掺杂二氧化硅光纤预制棒的表面晶化

Surface Crystallization in F and P Co-doped Silica Fiber Preform
作者单位
1 北京交通大学 理学院物理系,北京 100044
2 悉尼大学光纤技术中心,悉尼 1430
摘要
对F、P共掺杂光纤预制棒退火后的表面晶化行为进行了研究.由改进的化学汽相沉淀法制备的氟和磷共掺杂二氧化硅光纤预制棒玻璃样品在6 h的1 150 ℃控温加热处理后,其表面发生晶化.用X-射线衍射仪观测其晶相,主要为α-方石英,可使玻璃具有二阶光学非线性;用光学显微镜观察了其表面形貌并对结晶微粒的大小进行测量,知晶粒大小在十几到几十μm之间,会造成散射损耗的增加.实验结果,还显示氟对结晶过程有很大的影响.
Abstract
Surface crystallization was observed in fluorine and phosphorous co-doped fused silica samples from an optical fiber preform fabricated by modified chemical vapor deposition method after being heated at 1 150 ℃ for 6 h.X-ray diffraction was utilized to investigate the crystalline phase,which was measured to be α-cristobalite,which made the glass own second-order nonlinearity.The glass surface after heating was inspected under an optical microscope and the size of individual crystalline particles was measured.The size of the crystal particle may be around dozens micron,and may result in a lot scattering loss for optical transmission.It is shown that the doped F plays an important role in the surface crystallization process.

戎根苗, 唐莹, 衣立新, 吕燕伍, 安宏林. 氟磷共掺杂二氧化硅光纤预制棒的表面晶化[J]. 光子学报, 2009, 38(5): 1101. RONG Gen-miao, TANG Ying, YI Li-xin, Lv Yan-wu, AN Hong-lin. Surface Crystallization in F and P Co-doped Silica Fiber Preform[J]. ACTA PHOTONICA SINICA, 2009, 38(5): 1101.

关于本站 Cookie 的使用提示

中国光学期刊网使用基于 cookie 的技术来更好地为您提供各项服务,点击此处了解我们的隐私策略。 如您需继续使用本网站,请您授权我们使用本地 cookie 来保存部分信息。
全站搜索
您最值得信赖的光电行业旗舰网络服务平台!