Nd∶Y3Al5O12单晶及纳米粉体的Raman光谱分析

Raman Spectra Analysis of Nd∶YAG Single Crystal and Its Nano-Powder

  • 摘要
  • 论文信息
  • 参考文献
  • 被引情况
  • PDF全文
分享:

摘要

测量了YAG(Y3Al5O12)/Nd∶YAG单晶、 Nd∶YAG前驱物及其在不同温度下煅烧获得粉体的拉曼光谱, 对谱峰的振动模式进行了指认, 对结果进行了分析。 Nd∶YAG前驱物在煅烧时, 有一个由非晶态向晶态的转化过程; 700 ℃下烧结前驱物获得非晶态产物的结构中含有AlO4四面体结构; 随着煅烧温度的升高, 拉曼光谱的变化主要表现在两个方面: 一是谱峰半高宽(FWHM)减小, 谱峰强度增大; 二是一些拉曼光谱谱峰发生了频移, 这是纳米多晶粉体的界面组元的有序度提高所致。 另外, 800 ℃下煅烧获得的Nd∶YAG纳米粉体的晶格振动模式与Nd∶YAG晶体的晶格振动模式存在差异, 这是纳米多晶粉体的界面组元的贡献所致。

Abstract

In the present paper, the authors measured the Raman spectra of YAG/Nd∶YAG single crystal, Nd∶YAG precursor and the powder sintered at different temperatures. The bands of these Raman spectra were assigned and analyzed. The results show that there is a structure transformation process in the course of sintering Nd∶YAG precursor. The powder sintered at 700 ℃ was amorphous and it is of AlO4 tetrahedron structure. With the increase in sintering temperatures, the Raman spectra varied mainly in two respects. One is the decrease in FWHM with the increase in the bands intensity; the other is the bands shift. These should be due to the increase in the order degree of the interface component. Additionally, the difference in the lattice vibration modes between the powders sintered at 800 ℃ and the Nd∶YAG single crystal powder was caused by the contribution of the interface component.

Newport宣传-MKS新实验室计划
补充资料

中图分类号:O657.3

基金项目:国家自然科学基金项目(10804053, 60478025)和南京信息工程大学校科研基金项目资助

收稿日期:2008-02-12

修改稿日期:2008-05-16

网络出版日期:0001-01-01

作者单位    点击查看

苏静:南京信息工程大学数理学院, 江苏 南京 210044
张庆礼:中国科学院安徽光学精密机械研究所, 安徽 合肥 230031
殷绍唐:中国科学院安徽光学精密机械研究所, 安徽 合肥 230031
孙敦陆:中国科学院安徽光学精密机械研究所, 安徽 合肥 230031
邵淑芳:中国科学院安徽光学精密机械研究所, 安徽 合肥 230031

联系人作者:苏静(sj007@163.com)

备注:苏静, 女, 1978年生, 南京信息工程大学材料物理系讲师

【1】Ikesue A, Kinoshita T, Kamata K, et al. J. Am. Ceram. Soc., 1995, 78(4): 1033.

【2】Lu J R, Prabhu M, Xu J, et al. Appl. Phys. Lett., 2000, 77 (23): 3707.

【3】Lu J R, Prabhu M, Ueda K, et al. Laser Physics, 2001, 11: 1053.

【4】Lu J R, Ueda K, Yagi H, et al. Journal of Alloys and Compounds, 2002, 341: 220.

【5】Hurrell J P, Porto S P S, Chang I F, et al. Phys. Rev., 1968, 173(3): 851.

【6】Wadsack R L, Lewis Joan L, Argyle B E. Phys. Rev. B, 1971, 3(12): 4342.

【7】Papagelis K, Kanellis G, Ves S, et al. Phys. Stat. Sol. (b), 2002, 233(1): 134.

【8】Chen Y F, Lim P K, Lim S J, et al. J. Raman Spectrosc., 2003; 34: 882.

【9】SU Jing, ZHANG Qing-li, GU Chang-jiang, et al(苏静, 张庆礼, 谷长江, 等). Journal of Functional Materials(功能材料), 2005, 36(5): 717.

【10】Kato S, Iga T, Hatano S, et al. Yogyo-Kyokai-Shi., 1976, 84(5): 215.

【11】Saito N, Matsuda S, Ikegami T. J. Am. Ceram. Soc., 1998, 81(8): 2023.

【12】Sordelet D J, Akinc M. Colloids Int. Sci., 1988, 122(1): 47.

【13】Morgan H W, Staats P A. J. Applied Physics, 1962, 33: 364.

【14】HOU Huai-yu, YOU Jing-lin, WU Yong-quan, et al(侯怀宇, 尤静林, 吴永全, 等). Chinese Journal of Light Scatting(光散射学报), 2001, 13(3): 162.

【15】Alben R, Weaire D, Smith Jr J E, et al. Phys. Rev. (B), 1975, 11(6): 2271.

【16】SUN Ping, XIONG Bo, ZHANG Guo-qing, et al(孙萍, 熊波, 张国青, 等). Spectroscopy and Spectral Analysis(光谱学与光谱分析), 2007, 27(1): 143.

【17】ZHANG Zhong-suo, ZHANG Xing-tang, CHEN Yan-hui, et al(张忠锁, 张兴堂, 陈艳辉, 等). Spectroscopy and Spectral Analysis(光谱学与光谱分析), 2003, 23(1): 98.

【18】WU Zheng-kai, TANG Ao-qing(吴征铠, 唐敖庆). Monograph of Molecular Spectroscopy(分子光谱专论). Ji’nan: Shandong Scientific and Technology Press(济南: 山东科技出版社), 1999. 2129.

【19】ZHANG Li-de, MOU Ji-mei(张立德, 牟季美). Nano-Materials and Nano-Structures(纳米材料和纳米结构). Beijing: Science Press(北京: 科学出版社), 2001. 227.

引用该论文

SU Jing,ZHANG Qing-li,YIN Shao-tang,SUN Dun-lu,SHAO Shu-fang. Raman Spectra Analysis of Nd∶YAG Single Crystal and Its Nano-Powder[J]. Spectroscopy and Spectral Analysis, 2009, 29(6): 1577-1580

苏静,张庆礼,殷绍唐,孙敦陆,邵淑芳. Nd∶Y3Al5O12单晶及纳米粉体的Raman光谱分析[J]. 光谱学与光谱分析, 2009, 29(6): 1577-1580

您的浏览器不支持PDF插件,请使用最新的(Chrome/Fire Fox等)浏览器.或者您还可以点击此处下载该论文PDF