发光学报, 2010, 31 (4): 489, 网络出版: 2010-08-31   

绿色长余辉材料 MgAl2O4∶Mn2+的合成及其发光特性

Synthesis and Luminescent Properties of Green Long-lasting Phosphorescent Materials MgAl2O4∶Mn2+
作者单位
1 中国科学院 长春光学精密机械与物理研究所 激发态物理重点实验室, 吉林 长春130033
2 中国科学院 研究生院, 北京100039
3 东北大学 秦皇岛分校, 河北 秦皇岛 066004
摘要
采用高温固相法在1 350 ℃下合成了Mn2+掺杂的MgAl2O4发光材料, 利用X射线衍射对所合成样品的结构进行了表征。用209 nm的紫外灯照射样品后, 观察到来自Mn2+的4T1-6A1跃迁的绿色长余辉发光。发光的激发光谱表明:Mn2+-3d组态内存在一系列强的激发峰, 分别在279, 361, 386, 427, 451 nm, 同时还有209 nm处的Mn-O电荷迁移带, 激发该吸收带会产生很强的绿色余辉。测量了余辉的衰减曲线及热释光谱, 分析了Mn2+掺杂浓度对样品余辉性质的影响, 给出了余辉产生的可能模型。
Abstract
Green long persistent phosphors of MgAl2O4∶Mn2+ were synthesized at high temperature under weak reductive atmosphere. The XRD pattern of the sample shown that the product is the simple MgAl2O4 phase. Photoluminescence (PL) excitation and emission, long-lasting phosphorescent (LLP) emission, decay curves, and thermostimulated-luminescence (TSL) spectra were used to characterize the powder phosphor. The sample emits green LLP emission at about 520 nm [Mn2+-4T1(4G)→6A1(6S)] when excited by 209 nm. There are two ways of excitation energy: (1)Mn2+ ions is excited directly under UV excitation between 279 nm and 451 nm, resulting in green photoluminescence; (2)For 209 nm excitation, Mn2+ ionscharge transfer transition exists, so the electrons from the Mn2+ ground state 6A1 are excited to the conduction band (CB). On one hand, the electrons in the CB can relax to the excited states of Mn2+ through nonradiative processes, and then is green emission followed. On the other hand, some of the electrons in the CB can also be trapped in the electron traps, and then released at high temperature, then turned to the excited states of Mn2+ through nonradiative processes, leading to the phenomenon of green LLP of Mn2+. The possible mechanism for this phenomenon of green LLP of MgAl2O4∶Mn2+ is also investigated based on the experimental results.

张燕, 钟瑞霞, 张霞, 任新光, 郝振东, 张家骅. 绿色长余辉材料 MgAl2O4∶Mn2+的合成及其发光特性[J]. 发光学报, 2010, 31(4): 489. ZHANG Yan, ZHONG Rui-xia, ZHANG Xia, REN Xin-guang, HAO Zhen-dong, ZHANG Jia-hua. Synthesis and Luminescent Properties of Green Long-lasting Phosphorescent Materials MgAl2O4∶Mn2+[J]. Chinese Journal of Luminescence, 2010, 31(4): 489.

本文已被 1 篇论文引用
被引统计数据来源于中国光学期刊网
引用该论文: TXT   |   EndNote

相关论文

加载中...

关于本站 Cookie 的使用提示

中国光学期刊网使用基于 cookie 的技术来更好地为您提供各项服务,点击此处了解我们的隐私策略。 如您需继续使用本网站,请您授权我们使用本地 cookie 来保存部分信息。
全站搜索
您最值得信赖的光电行业旗舰网络服务平台!