竹节状α-Fe2O3纳米棒的制备、表征和性能研究

Preparation, Characterization and Property of Bamboo-Like α-Fe2O3 Nanobars
作者单位
1 中南大学粉末冶金国家重点实验室, 湖南 长沙 410083
2 长沙理工大学物理与电子科学学院, 湖南 长沙 410076
摘要
以硝酸铁为铁源,氨水为沉淀剂,聚乙二醇(PEG)为分散剂,采用共沉淀法制备氢氧化铁前驱体,然后将获得的前驱体在450℃、氮气保护下热处理2h,最后利用透射电镜、X射线衍射、拉曼光谱和近边X射线精细结构光谱(NEXAFs)表征样品的形貌和结构,并使用HH-50型振动样品磁强计测量样品在室温下的磁学行为。透射电镜结果显示,获得的样品由氧化铁纳米颗粒和竹节状氧化铁纳米棒组成,纳米颗粒的粒径范围为50-100nm,纳米棒的直径大约为10nm。XRD表征显示样品中氧化铁纳米棒和纳米颗粒为赤铁矿型α-Fe2O3;光谱实验结果证实了样品中氧化铁纳米颗粒和纳米棒的结构是α-Fe2O3;磁学性能测试表明获得的样品表现为典型铁磁性材料的磁滞回线,其饱和磁感应强度约为64.65emu·g^-1,矫顽力的大小约为15.13Oe。
Abstract
Firstly, hydroxide iron precursor was prepared by the co-precipitation method through using nitric iron as the source of iron, ammonia as precipitants, and poly-glycol as dispersant. Secondly, the precursor was calcined at 450 ℃ for 2 h under the protection of nitrogen. Finally, the images and structures of resultant powders were investigated by transmission electron microscopes (TEM), X-ray diffraction (XRD), Raman spectrum and the near-edge X-ray absorption fine structure (NEXAFS), respectively, and the magnetic property of resultant powders was measured by a vibrating sample magnetometer (VSM HH-50). The experimental results of TEM show that the products are composed of Fe2O3 nano-particles with sizes in the range of 50-100 nm and bamboo-like Fe2O3 nanobars about 10 nm in diameter. The experimental results of XRD and spectrum illuminate that the structures of products are a-Fe2O3. Moreover, magnetic properties measurement reveals that the products exhibit typical magnetic hysteresis loops of ferromagnetism materials, and their saturation magnetization and coercive force are approximately 64. 65 emu · g^-1 and 15.13 Oe, respectively.

陈传盛, 刘咏, 黄伯云, 雷霆, 陈小华. 竹节状α-Fe2O3纳米棒的制备、表征和性能研究[J]. 光谱学与光谱分析, 2009, 29(10): 2871. CHEN Chuan-sheng, LIU Yong, HUANG Bai-yun, LEI Ting, CHEN Xiao-hua. Preparation, Characterization and Property of Bamboo-Like α-Fe2O3 Nanobars[J]. Spectroscopy and Spectral Analysis, 2009, 29(10): 2871.

关于本站 Cookie 的使用提示

中国光学期刊网使用基于 cookie 的技术来更好地为您提供各项服务,点击此处了解我们的隐私策略。 如您需继续使用本网站,请您授权我们使用本地 cookie 来保存部分信息。
全站搜索
您最值得信赖的光电行业旗舰网络服务平台!