发光学报, 2010, 31 (5): 732, 网络出版: 2011-02-15
白光LED用Eu2+离子激活含氮铝酸盐发光粉的制备
Preparation of Eu2+-activated Aluminate Doped by N Phosphors for White LED
摘要
采用高温固相反应法制备Sr3Al2O6-3x/2Nx∶ Eu2+发光材料。发光光谱分析表明, 该材料在400~550 nm可见光激发下, 发射光谱为峰值波长为600 nm的宽带谱。XRD分析结果显示, Sr3Al2O6-3x/2Nx与Sr3Al2O6的晶体结构相同。研究了Eu2+离子浓度对材料发光性能的影响, 结果表明随着Eu2+离子浓度的增加, 材料的发光强度呈现出先增强后减弱的趋势, 当Eu2+浓度为15%时, 发光强度最大。根据Dexter理论, 其浓度猝灭机理是电四极-电四极的相互作用。引入Ce3+作为敏化剂, 样品的发光强度明显增强。
Abstract
The Sr3Al2O6-3x/2Nx∶Eu2+ phosphor was synthesized by solid-state reaction method. The study of Sr3Al2O6-3x/2Nx∶Eu2+ spectra indicated that the emission spectra was the broad band spectra peaking at 600 nm when exciting at 400~550 nm. The XRD results showed that the crystal structure of Sr3Al2O6-3x/2Nx∶Eu2+ was the same as Sr3Al2O6. Effect of Eu2+ concentration on luminescent intensity of Sr3Al2O6-3x/2Nx∶Eu2+ phosphor was investigated. The results showed that the luminescent intensity firstly increased with increasing Eu2+ content and then decreases. The Eu2+ content corresponding to the maximal luminescent intensity is 15%. According to Dexter theory, the concentration quenching mechanisms are the q-q (quadrupole-quadrupole) interaction. The emission intensity of Sr3Al2O6-3x/2Nx∶Eu2+,Ce3+ is higher than that of the other phosphor activated by Eu2+ only.
柏朝晖, 张希艳, 朱宏苑, 张舒婷, 吕建军, 周晓宸. 白光LED用Eu2+离子激活含氮铝酸盐发光粉的制备[J]. 发光学报, 2010, 31(5): 732. BAI Zhao-hui, ZHANG Xi-yan, ZHU Hong-yuan, ZHANG Shu-ting, LU Jian-jun, ZHOU Xiao-chen. Preparation of Eu2+-activated Aluminate Doped by N Phosphors for White LED[J]. Chinese Journal of Luminescence, 2010, 31(5): 732.