光子学报, 2011, 40 (2): 217, 网络出版: 2011-03-08
远红外Ge-Te-AgI硫卤玻璃光学性能
Optical Properties of Ge-Te-AgI Far Infrared Chalco-halide Glasses
硫卤玻璃 光学性能 光学带隙 红外透过谱 Chalco-halide glasses Optical properties Optical band gap Infrared transmission spectrum
摘要
用传统熔融淬冷法制备了一系列(100-x)(GeTe4.3)-xAgI (x=5, 10, 20, 30)硫卤玻璃.并通过阿基米德法、XRD衍射、差热分析、可见/近红外吸收光谱、红外透射光谱等手段研究了该硫卤玻璃的热稳定性和光学特性.研究表明随着AgI含量的增加,玻璃的密度从5.591 g·cm-3递增到6.314 g·cm-3;折射率从3.73上升到5.70;XRD衍射数据表明该玻璃体系在较宽的组分范围内没有微晶析出,说明成玻范围较宽;差热分析表明当x=5时玻璃有着最高的转变温度206 ℃;AgI含量增多时短波截止限发生红移,红外截止波长基本不变(均超过25 μm),表明此硫卤玻璃材料在远红外领域有很大的潜在应用前景.
Abstract
A series of (100-x)(GeTe4.3)-xAgI(x=5, 10, 20, 30)chalcogenide glasses were prepared by traditional melt-quenching method. The density was obtained by the Archimedes principle. The thermal property was analyzed by XRD diffraction and DTA curves. The optical property was analyzed by UV-VIS-NIR absorption spectrum and Infrared transmission spectrum, respectively. The results show that with the increasing of AgI content, the density of the glasses increases from 5.591 g·cm-3 to 6.314 g·cm-3 and the glass system has high refractive index from 3.73 to 5.70. The glass samples are amorphous, resulting in a wide composition range of glass formation. A maximum glass transition temperatures value of Tg (206 ℃) was obtained for x=5. A red-shifting occurs in the short-wavelength absorption cutting-off edge and the infrared cut-off wavelength is nearly unchanged. The infrared transmission edge is beyond 25 μm, which provides an important candidate for the development of far-infrared Te-based chalcogenide glass materials.
白坤, 聂秋华, 王训四, 戴世勋, 沈祥, 王国祥. 远红外Ge-Te-AgI硫卤玻璃光学性能[J]. 光子学报, 2011, 40(2): 217. BAI Kun, NIE Qiu-hua, WANG Xun-Si, DAI Shi-xun, SHEN Xiang, WANG Guo-xiang. Optical Properties of Ge-Te-AgI Far Infrared Chalco-halide Glasses[J]. ACTA PHOTONICA SINICA, 2011, 40(2): 217.