中国激光, 2011, 38 (5): 0503001, 网络出版: 2011-05-09   

6061-T6铝合金高速高功率CO2激光填丝焊接性的研究 下载: 1370次

Research on High Speed High Power CO2 Laser Welding of 6061-T6 Aluminum with Filler Wire
作者单位
1 上海交通大学上海市激光制造与材料改性重点实验室, 上海 200240
2 上海飞机制造有限公司, 上海 200436
摘要
为实现6061-T6铝合金薄板的高速高功率CO2激光填丝焊接,选用了ER4043,ER5356两种焊丝进行了焊接性试验。利用鱼骨状试样对两种焊丝的激光焊接铝合金6061-T6的热裂纹敏感性进行了分析;利用金相显微镜、扫描电镜、显微硬度计以及万能材料试验机分析了焊接接头的组织与性能。研究结果表明,与填充ER5356焊丝相比,填充ER4043焊丝的焊接接头热裂纹敏感性较低,焊接速度可达6 m/min。焊缝主要是柱状晶、等轴晶及少量树枝晶,显微硬度在60~80 HV,拉伸强度可达240~262 MPa,弯曲性能良好。
Abstract
In order to realize the high power CO2 laser welding of 6061-T6 aluminum alloy sheet under high travel speed, filler wire ER4043 and ER5356 are selected for welding. In the experiments, welding hot cracking sensitivity is analyzed by use of fishbone samples, and optical microscope, scanning electron microscope, micro-hardness test and mechanical property test are applied to analyze the microstructure and properties of the joints. Results indicate that compared with filling wire ER5356, the hot crack sensibility of the joint welded with wire ER4043 is lower, and a maximal welding speed of 6 m/min can be reached. The weld contains columnar grains, equiaxes grains, and some dendrites grains. The weld has a micro-hardness of joint with ER4043 of 60~80 HV, a tensile strength of 240~262 MPa and a good bending property.

翟玉峰, 黄坚, 李敏, 陈洁, 杨模聪, 赵勇. 6061-T6铝合金高速高功率CO2激光填丝焊接性的研究[J]. 中国激光, 2011, 38(5): 0503001. Zhai Yufeng, Huang Jian, Li Min, Chen Jie, Yang Mocong, Zhao Yong. Research on High Speed High Power CO2 Laser Welding of 6061-T6 Aluminum with Filler Wire[J]. Chinese Journal of Lasers, 2011, 38(5): 0503001.

本文已被 13 篇论文引用
被引统计数据来源于中国光学期刊网
引用该论文: TXT   |   EndNote

相关论文

加载中...

关于本站 Cookie 的使用提示

中国光学期刊网使用基于 cookie 的技术来更好地为您提供各项服务,点击此处了解我们的隐私策略。 如您需继续使用本网站,请您授权我们使用本地 cookie 来保存部分信息。
全站搜索
您最值得信赖的光电行业旗舰网络服务平台!