纳秒脉冲下聚合物电树枝引发实验方法

Experimental method of electrical tree initiation in polymer under high voltage nanosecond pulses

  • 摘要
  • 论文信息
  • 参考文献
  • 被引情况
  • PDF全文
分享:

摘要

借鉴直流、交流的研究经验, 比较了纳秒脉冲条件下几种不同的电树枝老化实验方法。对单针-板电极和多针-板电极在纳秒脉冲下实验结果的一致性进行考察, 结果表明,多针-板电极系统可以在提高实验效率的同时保证结果的准确性。采用步进法和累加法进行了不同频率下聚苯乙烯电树枝引发实验,结果表明:两种方法得到的纳秒脉冲下聚苯乙烯电树枝引发电压-频率特性基本一致, 在50~500 Hz范围内, 引发电压随频率的升高而降低;在500~800 Hz范围内, 引发电压随频率的升高而增加。最后讨论了对于不同脉冲功率装置中绝缘材料老化试验设计的方法。

Abstract

The point-plane geometry with iron electrode system was employed in the electrical tree initiation experiment under high voltage nanosecond pulses, with both single and multiple needle electrodes. The result of the latter electrode scheme has a good correlation with that of the former, with higher efficiency at the mean time. Electrical tree initiation experiments were done by the step-up method and accumulation method at different frequencies, and the initiation characteristics of polystyrene were derived. The initiation voltage drops as the pulse frequency rises up from 50 Hz to 500 Hz, while it increases as the frequency rises in the range of 500 Hz to 800 Hz. Aging experiments for different pulsed power utilities were also designed.

补充资料

中图分类号:TM855

所属栏目:脉冲功率技术

基金项目:国家自然科学基金重点项目(50437020);国家自然科学基金项目(50907068);清华大学电力系统及发电设备控制和仿真国家重点实验室开放基金项目(SKLD09KM15)

收稿日期:2010-07-01

修改稿日期:2010-10-22

网络出版日期:--

作者单位    点击查看

张伟:中国科学院 电工研究所, 北京 100190中国科学院 电力电子与电气驱动重点实验室, 北京 100190中国科学院 研究生院, 北京 100049
王珏:中国科学院 电工研究所, 北京 100190中国科学院 电力电子与电气驱动重点实验室, 北京 100190
张东东:中国科学院 电工研究所, 北京 100190中国科学院 电力电子与电气驱动重点实验室, 北京 100190
欧阳文敏:中国科学院 电工研究所, 北京 100190中国科学院 电力电子与电气驱动重点实验室, 北京 100190中国科学院 研究生院, 北京 100049
严萍:中国科学院 电工研究所, 北京 100190中国科学院 电力电子与电气驱动重点实验室, 北京 100190
高迎慧:中国科学院 电工研究所, 北京 100190中国科学院 电力电子与电气驱动重点实验室, 北京 100190

联系人作者:张伟(zhangwei@mail.iee.ac.cn)

备注:张伟(1986—), 男, 硕士研究生, 研究方向为高电压绝缘技术

【1】Tanaka T. Charge transfer and tree initiation in polyethylene subjected to AC voltage[J]. IEEE Trans on Electrical Insulation, 1992, 27(3):424-431.

【2】郑晓泉,Chen G.机械应力与电压频率对XLPE电缆电树枝的影响[J].高电压技术, 2003, 29(4):6-8.(Zheng Xiaoquan, Chen G. Structures and propagation characteristics of electrical trees in XLPE cable insulation. High Voltage Engineering, 2003, 29(4):6-8)

【3】周远翔, 王珣, 邱东刚, 等.热处理对聚乙烯形态及其电树起始电压的影响[J].绝缘材料, 2001, 34(4):34-37.(Zhou Yuanxiang, Wang Xun, Qiu Donggang, et al. Annealing effect on the morphology of polyethylene materials and the tree initiation voltage. Insulating Materials, 2001, 34(4):34-37)

【4】王珏, 任成燕, 严萍, 等.ns脉冲下有机玻璃电树枝的引发特性[J].高电压技术, 2009, 35(1):120-124.(Wang Jue, Ren Chengyan, Yan Ping, et al. Initial characteristics of electrical tree in PMMA under repetitive nanosecond pulses. High Voltage Engineering, 2009, 35(1):120-124)

【5】欧阳文敏, 王珏, 张东东, 等.重复频率脉冲下环氧树脂电树枝引发特性[J].强激光与粒子束, 2010, 22(6):1378-1382.(Ouyang Wenmin, Wang Jue, Zhang Dongdong, et al. Electrical tree initiation characteristics under repetitive pulse in epoxy resin. High Power Laser and Particle Beams, 2010, 22(6):1378-1382)

【6】Dissado L A, Fothergill J C. Electrical degradation and breakdown in polymers[M]. London: Peter Peregrinus Ltd, 1992.

【7】李盛涛,郑晓泉.聚合物电树枝化[M].北京:机械工业出版社, 2006.(Li Shengtao, Zheng Xiaoquan. Electrical tree of polymer. Beijing: China Machine Press, 2006)

【8】任浩.重频纳秒脉冲下有机玻璃电树枝老化特性的研究[D].北京:中国科学院研究生院, 2008.(Ren Hao. Research on electrical tree phenomenon in PMMA under repetitive nanosecond high electrical field pulse. Beijing: Graduate University of Chinese Academy of Sciences, 2008)

【9】Zhang Dongdong, Yan Ping, Wang Jue. Simulation on a magnetic pulse compression system for DWA[C]//1st Euro-Asian Pulsed Power Conference. 2006.

【10】刘平原, 贺景亮, 邰淑彩.交联聚乙烯绝缘老化的试验与建模研究[J].绝缘材料, 2002, 35(1):21-23.(Liu Pingyuan, He Jingliang, Tai Shucai. Study on experiment and modeling in electrical tree aging of XLPE insulation. Insulating Materials, 2002, 35(1):21-23)

【11】邓奕光, 侯宇军.复合绝缘子护套材料在雾室中的加速老化试验[J].电瓷避雷器, 1992, (5):44-48.(Deng Yiguang, Hou Yujun. Accele-rated life test of composite insulator sheath insulation material in spray chamber. Insulators and Surge Arresters, 1992, (5):44-48)

【12】李凌, 徐伟.密封式电磁继电器步进应力加速寿命试验的分析方法[J].低压电器, 2010, (1):5-7.(Li Ling, Xu Wei. Analysis approach for step-stress accelerated life test of sealed magnetic relays. Low Voltage Apparatus, 2010, (1):5-7)

【13】湛远礼, 罗红.恒定应力加速寿命试验模型及应用——威布尔分布[J].自动化与仪器仪表, 2009, (6):48-54.(Zhan Yuanli, Luo Hong. Constant stress accelerated life test model and its application—Weibull distribution. Automation and Instrumentation, 2009, (6):48-54)

【14】陈少卿, 成霞, 王霞, 等.聚合物中空间电荷的研究[J].绝缘材料, 2007, 40(4):48-52.(Chen Shaoqing, Cheng Xia, Wang Xia, et al. Research of space charge in polymer. Insulating Materials, 2007, 40(4):48-52)

【15】杨强, 安振连, 郑飞虎, 等.线性低密度聚乙烯中空间电荷陷阱的能量分布与空间电荷分布的关系[J].物理学报, 2008, 57(6):3834-3839.(Yang Qiang, An Zhenlian, Zheng Feihu, et al. The relationship between energy distribution and space distribution of charge traps in linear low density polyethylene. Acta Physica Sinica, 2008, 57(6):3834-3839)

【16】周远翔, 聂琼, 姜绿先, 等.针尖曲率半径对硅橡胶电树枝老化特性的影响[J].中国电机工程学报, 2008, 28(34):27-36.(Zhou Yuanxiang, Nie Qiong, Jiang Lüxian, et al. Influence of curvature radius of needle tip on characteristics of electrical treeing in silicone rubber. Proceedings of the CSEE, 2008, 28(34):27-36)

引用该论文

Zhang Wei,Wang Jue,Zhang Dongdong,Ouyang Wenmin,Yan Ping,Gao Yinghui. Experimental method of electrical tree initiation in polymer under high voltage nanosecond pulses[J]. High Power Laser and Particle Beams, 2011, 23(4): 1117-1122

张伟,王珏,张东东,欧阳文敏,严萍,高迎慧. 纳秒脉冲下聚合物电树枝引发实验方法[J]. 强激光与粒子束, 2011, 23(4): 1117-1122

您的浏览器不支持PDF插件,请使用最新的(Chrome/Fire Fox等)浏览器.或者您还可以点击此处下载该论文PDF