应用激光, 2011, 31 (2): 130, 网络出版: 2011-07-01   

铝合金T型接头激光双侧填丝焊接工艺研究

Experimental Properties Study on Both-Side Laser Beam Welding of T-joint Aluminum Alloy
作者单位
1 国家商用飞机制造工程技术研究中心, 上海 200436
2 哈尔滨工业大学先进焊接与连接国家重点实验室, 黑龙江 哈尔滨 150001
摘要
以 2 mm厚 6056铝合金为试验材料, 采用激光双侧填丝焊接方法进行铝合金 T型接头焊接工艺试验, 主要研究了光束入射角度、光束入射位置、送丝速度与焊接速度等工艺参数对焊缝成形的影响; 分析了 T型接头焊缝的显微组织特征与拉伸性能。试验结果表明: 光束入射角度过大时, 两侧焊缝重合面积较小且蒙皮热变形较大; 当光束入射位置偏移立筋 0.2~0.3 mm时可以显著改善蒙皮背部的热变形。焊缝中心组织与两侧无明显差别, 均为细小的等轴晶。焊缝熔深是 T型接头拉伸载荷的重要影响因素, 接头起裂于蒙皮焊趾处, 断裂于焊缝与母材金属之间的熔合区。
Abstract
The experiment of both-side laser beam welding with filling wire of T-joint aluminum alloy was carried out. The effects ofbeam incident angle and position, wire feed speed and welding speed on the weld appearance were investigated. The microstructurecharacteristic and tensile property of T -joint were analyzed. The experimental results show that the weld appearance was mostinfluenced by the beam incident angle and position. It indicated that the weld overlap area was small and the skin distortion wasserious when the laser incident angle was in high level. The skin distortion was small when the laser position deviated 0.2~0.3 mm on the vertical board. The weld microstructure was equiaxed grains and had no significant difference between weld center and edge.The fillet weld penetration was the key controlling factors of T-joint tensile load. The specimen failed at weld toe, and fractured alongthe fusion layer between base metal and weld metal.

陈洁, 杨志斌, 占小红, 王玉华, 陈彦宾. 铝合金T型接头激光双侧填丝焊接工艺研究[J]. 应用激光, 2011, 31(2): 130. Chen Jie, Yang Zhibin, Zhan Xiaohong, Wang Yuhua, Chen Yanbin. Experimental Properties Study on Both-Side Laser Beam Welding of T-joint Aluminum Alloy[J]. APPLIED LASER, 2011, 31(2): 130.

本文已被 2 篇论文引用
被引统计数据来源于中国光学期刊网
引用该论文: TXT   |   EndNote

相关论文

加载中...

关于本站 Cookie 的使用提示

中国光学期刊网使用基于 cookie 的技术来更好地为您提供各项服务,点击此处了解我们的隐私策略。 如您需继续使用本网站,请您授权我们使用本地 cookie 来保存部分信息。
全站搜索
您最值得信赖的光电行业旗舰网络服务平台!