中国激光, 2012, 39 (5): 0503005, 网络出版: 2012-05-02   

镀锌钢激光添粉焊接的等离子体监测机理

Monitoring Mechanism of Plasma Generated by Laser Welding Galvanized Steel with Powder Feeding
作者单位
1 湖南大学 汽车车身先进设计制造国家重点实验室, 湖南 长沙 410082
2 大连理工大学 材料科学与工程学院, 辽宁 大连 116024
摘要
采用CO2激光器对1.6 mm厚的B340/590DPD+Z镀锌钢板间添加不同量铜粉进行了激光搭接焊。基于光谱仪采集的焊接等离子体光信号,分析添加铜粉对焊接过程产生的等离子体光信号的影响,以及焊接气孔与等离子体光信号的关系。焊后采用扫描电子显微镜(SEM)及能谱仪(EDS)对焊缝截面扫描,检测铜元素的平均含量及气孔内壁主要元素的分布变化。研究结果表明,添加铜粉较未添加铜粉激光搭接焊时,等离子体温度振荡显著降低,平均温度下降约5000 K;气孔内壁存在着铜锌固溶体合金,且焊缝中的气孔缺陷与CuI324.8 nm谱线强度存在着关联。此结果为镀锌钢添加粉末激光焊接监测提供了理论依据,并为等离子体控制技术提供了一种新的方法。
Abstract
Experiments of laser welding of 1.6 mm thick galvanized steel B340/590DPD+Z with different amounts of copper are performed by using a CO2 laser. Based on the light emission from the plasma plume acquired by spectrometer in the welding process, the effects of adding copper powder on the plasma optical signal and the relationship between the pores and the plasma optical signal is analyzed. Then the average content of copper element and the distribution of the main elements around the pores are detected by using a scanning electron microscope (SEM) and energy dispersive spectroscopy (EDS). The results show that compared to laser welding without adding copper powder, the oscillation of plasma temperature is significantly reduced and the average temperature drops about 5000 K. In addition the solid solution alloy of copper and zinc distributes around the pore wall and the porosity has a correlation with the intensity of spectrum at CuI324.8 nm as well. The researches provide a theoretical basis for monitoring on laser welding galvanized steel with powder feeding and a new method for the plasma control technology.

张屹, 段林勇, 周惦武, 李时春, 王存山. 镀锌钢激光添粉焊接的等离子体监测机理[J]. 中国激光, 2012, 39(5): 0503005. Zhang Yi, Duan Linyong, Zhou Dianwu, Li Shichun, Wang Cunshan. Monitoring Mechanism of Plasma Generated by Laser Welding Galvanized Steel with Powder Feeding[J]. Chinese Journal of Lasers, 2012, 39(5): 0503005.

本文已被 3 篇论文引用
被引统计数据来源于中国光学期刊网
引用该论文: TXT   |   EndNote

相关论文

加载中...

关于本站 Cookie 的使用提示

中国光学期刊网使用基于 cookie 的技术来更好地为您提供各项服务,点击此处了解我们的隐私策略。 如您需继续使用本网站,请您授权我们使用本地 cookie 来保存部分信息。
全站搜索
您最值得信赖的光电行业旗舰网络服务平台!