发光学报, 2012, 33 (5): 540, 网络出版: 2012-06-11   

刮涂法制备聚合物薄膜太阳能电池

Polymer Solar Cells Fabricated with Doctorblade Coating Technique
作者单位
中国科学院长春应用化学研究所 高分子化学与物理国家重点实验室, 吉林 长春130022
摘要
系统地研究了采用刮涂法制备聚合物薄膜太阳能电池时刮涂速度和基底温度对活性层厚度以及形貌的影响。当刮涂速度增加或者基底温度降低时,由于溶液粘度和表面张力的变化导致活性层厚度增加。与旋涂方法相比,刮涂方法制备的活性层薄膜具有更小的粗糙度和精细的相分离结构,从而减少了光伏电池的漏电流并提高了填充因子。利用刮涂方法制备的聚合物太阳能电池能量转换效率达到了4.2%。
Abstract
The poly(3hexylthiophene):[6,6]phenyl C61butyric acid methyl ester (P3HT∶PCBM) bulkheterojunction polymer solar cells fabricated with doctorblade coating were studied. It is found that the active layer thickness increases with increasing the coating speed or lowing substrate temperature, which is attributed to the changes of solution viscosity and surface tension. Moreover, the P3HT∶PCBM active layer produced by doctorblade coating demonstrates fine donoracceptor nanoscale phase separation favoring enhancing exciton dissociation and charge collection. A 4.2% P3HT∶PCBM solar cell was fabricated with doctorblade coating technique.

吴江, 谢志元. 刮涂法制备聚合物薄膜太阳能电池[J]. 发光学报, 2012, 33(5): 540. WU Jiang, XIE Zhiyuan. Polymer Solar Cells Fabricated with Doctorblade Coating Technique[J]. Chinese Journal of Luminescence, 2012, 33(5): 540.

本文已被 1 篇论文引用
被引统计数据来源于中国光学期刊网
引用该论文: TXT   |   EndNote

相关论文

加载中...

关于本站 Cookie 的使用提示

中国光学期刊网使用基于 cookie 的技术来更好地为您提供各项服务,点击此处了解我们的隐私策略。 如您需继续使用本网站,请您授权我们使用本地 cookie 来保存部分信息。
全站搜索
您最值得信赖的光电行业旗舰网络服务平台!