光子学报, 2012, 41 (6): 728, 网络出版: 2012-06-19   

不同条件制备的ZnO纳米梳结构及其性能研究

Preparation and Properties of the ZnO Nanocombs
作者单位
南阳师范学院 物理与电子工程学院,河南 南阳 473061
摘要
采用热蒸发法通过改变衬底放置条件在Si (111)衬底上制备出了ZnO纳米梳结构.利用X射线衍射(XRD)、扫描电子显微镜(SEM)、分光光度计、场发射装置对样品的结构、形貌、光致发光光谱及场发射特性进行了分析.XRD结果表明衬底水平放置(A)和衬底竖直放置(B)制备出的样品均属于多晶六角纤锌矿结构.SEM结果表明两种衬底放置条件下的样品均为纳米梳状结构,改变衬底放置条件ZnO纳米梳的尺寸和形貌有明显改变,其中竖直放置衬底的样品B纳米尺寸较小且比较均匀.室温下的光致发光光谱表明样品B的紫外峰较样品A出现了蓝移,此外样品B的紫外峰强和可见光峰强比值较大,说明此样品的结晶质量较好.场发射特性测试结果表明两个样品的场发射都是通过电子隧道效应进行的,且样品B的场发射性能优于样品A.
Abstract
The ZnO nanocombs have been successfully synthesized on Si (111) substrates with different substrate placed conditions by thermal evaporation method. The XRD, SEM, specrophotometer and fieldemission testing device are used to investigate the morphology, structure, photoluminescence and field emission properties of the ZnO nanocombs. XRD results indicates that both of the two samples under different substrate placed conditions(A:horizontal and B:vertical)belong to polycrystalline hexagonal structure. SEM results show that both of the two samples have nanocomb structure, but the size and the surface morphology of the nanocombs change with the different substrates placed conditions. The nanocombs in sample B are smaller and uniform. The room temperature photoluminescence(PL) spectra results show that the UV emission peak of the sample B appears blueshift in comparison to that in sample A, and the ratio of the UV emission peak to the visible emission peak in sample B is larger, indicating the high crystallization quality. Besides, The field emission test results show that the field emission of the both two samples conduct through the electronic tunnel effect, and the field emission performance of sample B is better.

王爱华, 吕林霞, 宋海珍, 宋金璠, 包特木尔巴根, 卢成. 不同条件制备的ZnO纳米梳结构及其性能研究[J]. 光子学报, 2012, 41(6): 728. WANG Aihua, L Linxia, SONG Haizhen, SONG Jinfan, BAO Tmurbagan, LU Cheng. Preparation and Properties of the ZnO Nanocombs[J]. ACTA PHOTONICA SINICA, 2012, 41(6): 728.

本文已被 1 篇论文引用
被引统计数据来源于中国光学期刊网
引用该论文: TXT   |   EndNote

相关论文

加载中...

关于本站 Cookie 的使用提示

中国光学期刊网使用基于 cookie 的技术来更好地为您提供各项服务,点击此处了解我们的隐私策略。 如您需继续使用本网站,请您授权我们使用本地 cookie 来保存部分信息。
全站搜索
您最值得信赖的光电行业旗舰网络服务平台!