高温合金/不锈钢异种材料T型接头激光穿透焊工艺研究

Dissimilar Metals Combination of Superalloy/Stainless Steel in T-Shape by Laser Penetration Welding
作者单位
哈尔滨工业大学先进焊接与连接国家重点实验室, 黑龙江 哈尔滨 150001
摘要
针对飞行器发动机水冷壁结构,进行了GH3128/06Cr19Ni10异种材料T型接头激光穿透焊试验,主要研究了焊接参数对焊缝成形和焊接裂纹的影响规律,分析了焊接裂纹形成原因,得到了较合理的焊接工艺区间。结果表明,对于GH3128/06Cr19Ni10异种材料T型接头激光穿透焊,连续焊比脉冲焊更易实现稳定焊接,获得良好焊缝成形。焊接裂纹是接头主要缺陷裂纹都在高温合金一侧产生,控制激光功率、保证对中可降低裂纹产生概率。焊接接头的另一种缺陷是表面下塌,保证间隙小于0.2 mm可抑制下塌缺陷的产生。对由41条焊缝组成的模拟件进行了10 MPa,5 min水压测试,每条焊缝都满足要求。
Abstract
GH3128 and 06Cr19Ni10 which are mainly used in water wall of flight vehicle engine are joined together by laser penetration welding. The relationships between welding parameters and welding appearance and cracks are mainly researched. The reason of weld cracks is analyzed. A appropriate welding craft is summarized. The following conclusions are obtained. The continuous laser welding is better than pulse laser welding in terms of welding appearance and welding process stability. If the gap between the two metals is too big, the surface of the welding seam will collapse. The GH3128 plate may crack if the laser power is too high, or if the laser beam deviate from the centre. The welded specimen which contains 41 weld seams preform well at the hydrostatic test (10 MPa, 5 min).

冯威琦, 张云丰, 陶汪, 李俐群. 高温合金/不锈钢异种材料T型接头激光穿透焊工艺研究[J]. 中国激光, 2012, 39(10): 1003003. Feng Weiqi, Zhang Yunfeng, Tao Wang, Li Liqun. Dissimilar Metals Combination of Superalloy/Stainless Steel in T-Shape by Laser Penetration Welding[J]. Chinese Journal of Lasers, 2012, 39(10): 1003003.

本文已被 5 篇论文引用
被引统计数据来源于中国光学期刊网
引用该论文: TXT   |   EndNote

相关论文

加载中...

关于本站 Cookie 的使用提示

中国光学期刊网使用基于 cookie 的技术来更好地为您提供各项服务,点击此处了解我们的隐私策略。 如您需继续使用本网站,请您授权我们使用本地 cookie 来保存部分信息。
全站搜索
您最值得信赖的光电行业旗舰网络服务平台!