扫描方式对激光金属直接成形DZ125L高温合金薄壁件开裂的影响

Effect of Scanning Methods on the Cracking of the DZ125L Superalloy in Laser Direct Metal Forming

  • 摘要
  • 论文信息
  • 参考文献
  • 被引情况
  • PDF全文
分享:

摘要

为了消除激光金属直接成形DZ125L高温合金薄壁件中的裂纹,研究了激光扫描方式对薄壁件(单道多层)熔覆层应力分布和开裂的影响。对比了两种扫描方式(单向扫描和往复扫描)对薄壁件的应力分布和开裂的影响。模拟和实验结果表明,单向扫描方式下薄壁件的应力分布不均匀,引起薄壁件的两端出现严重的翘曲且中间部分出现裂纹;往复扫描方式下薄壁件的应力分布相当均匀,没有出现翘曲和裂纹,熔覆层表面比较平整。

Abstract

The effect of scanning methods on stress distribution and cracking of the DZ125L superalloy thin-wall structures is investigated numerically and experimentally. The results demonstrat that the stress distribution is not uniform in single-direction scanning method, which leads to warping in both sides of the structures and cracking in the middle regions. However, in back-and-forth scanning method, the stress distribution is relatively uniform, and the fabricated parts have smooth surface without any warping or cracking.

Newport宣传-MKS新实验室计划
补充资料

中图分类号:TG249;TG39

DOI:10.3788/cjl201239.1003002

所属栏目:激光制造

责任编辑:宋梅梅  信息反馈

基金项目:国家973计划(2007CB707704)和国家自然科学基金(51275392)资助课题。

收稿日期:2012-04-19

修改稿日期:2012-06-18

网络出版日期:--

作者单位    点击查看

Doan Tatkhoa:西安交通大学机械制造系统工程国家重点实验室, 陕西 西安 710049
李涤尘:西安交通大学机械制造系统工程国家重点实验室, 陕西 西安 710049
卢秉恒:西安交通大学机械制造系统工程国家重点实验室, 陕西 西安 710049
张安峰:西安交通大学机械制造系统工程国家重点实验室, 陕西 西安 710049
贺斌:西安交通大学机械制造系统工程国家重点实验室, 陕西 西安 710049
Do Xuantuoi:西安交通大学机械制造系统工程国家重点实验室, 陕西 西安 710049

联系人作者:Doan Tatkhoa(doankhoactm@gmail.com)

备注:Doan Tatkhoa(1980—),男,硕士研究生,主要从事激光金属直接成形方面的研究。

【1】Y. Huang, X. Zeng. Investigation on cracking behavior of Ni-based coating by laser-induction hybrid cladding[J]. Applied Surface Science, 2010, 256(20): 5985~5992

【2】Fujun Wang, Huaidong Mao, Dawei Zhang et al.. The crack control during laser cladding by adding the stainless steel net in the coating[J]. Applied Surface Science, 2009, 255(21): 8846~8854

【3】Ding Yangxi, Ouyang Zhiming. Influencing factors of the cladding layer cracks after laser cladding[J]. Materials Research and Application, 2008, 2(3): 211~214
丁阳喜, 欧阳志明. 激光熔覆层裂纹的影响因素[J]. 材料研究与应用, 2008, 2(3): 211~214

【4】Yang Ning, Yang Fan. Effect of laser cladding parameters on the quality of cladding layer[J]. Heat Treatment Technology and Equipment, 2010, 31(4): 17~19
杨宁, 杨帆. 激光熔覆工艺参数对熔覆层质量的影响[J]. 热处理技术与装备, 2010, 31(4): 17~19

【5】Zhao Hai′ou, Li Chunhua. Investigation on process and crack sensitivity during laser cladding[J]. Heat Treatment of Metals, 2001, (1): 18~21
赵海鸥, 李春华. 激光熔覆工艺特性及裂纹敏感性研究[J]. 金属热处理, 2001, (1): 18~21

【6】Zhu Gangxian, Zhang Anfeng, Li Dichen et al.. Study of carrier gas flow rate on forming quality of thin wall parts in laser metal direct manufacturing[J]. Applied Laser, 2009, 29(4): 275~281
朱刚贤, 张安峰, 李涤尘 等. 激光金属直接制造中载气流量对薄壁零件成形质量的研究[J]. 应用激光, 2009, 29(4): 275~281

【7】Zhu Gangxian, Zhang Anfeng, Li Dichen. Effect of process parameters on surface smoothness in laser cladding[J]. Chinese J. Lasers, 2010, 37(1): 296~301
朱刚贤, 张安峰, 李涤尘. 激光熔覆工艺参数对熔覆层表面平整度的影响[J]. 中国激光, 2010, 37(1): 296~301

【8】F. Huang, Z. Jiang, X. Liu et al.. Microstructure and properties of thin wall by laser cladding forming[J]. Journal of Materials Processing Technology, 2009, 209(11): 4970~4976

【9】Zhu Gangxian, Li Dichen, Zhang Anfeng et al.. Influence of deposited layer′s structure on flow field of coaxial powder feeding nozzle[J]. Chinese J. Lasers, 2010, 37(6): 1636~1642
朱刚贤, 李涤尘, 张安峰 等. 沉积层结构对同轴送粉喷嘴粉末流场的影响规律[J]. 中国激光, 2010, 37(6): 1636~1642

【10】Gangxian Zhu, Dichen Li, Anfeng Zhang et al.. Numerical simulation of metallic powder flow in a coaxial nozzle in laser direct metal deposition[J]. Opt. & Laser Technol., 2011, 43(1): 106~113

【11】Fu Chunxia, Jiang Jiang, Bian Xiufang et al.. Effects of heat treatment on microstructure and wear resistance of laser cladded Ni alloy coating[J]. Hot Working Technology, 2007, 36(15): 44~47
付春霞, 姜江, 边秀房 等. 热处理对激光熔覆Ni基合金层组织耐磨性的影响[J]. 热加工工艺, 2007, 36(15): 44~47

【12】Su Ronghua, Liu Weijun, Long Risheng. Effects of different substrate preheating temperature on temperature field during laser metal deposition shaping[J]. Journal of Engineering Design, 2009, 16(1): 44~49
苏荣华, 刘伟军, 龙日升. 不同基板预热温度对激光金属沉积成形过程温度场的影响[J]. 工程设计学报, 2009, 16(1): 44~49

【13】Su Ronghua, Long Risheng, Liu Weijun et al.. Effects of substrate preheating parts formed by laser temperature on microstructures of metal deposition shaping[J]. Journal of Engineering Design, 2009, 16(3): 210~216
苏荣华, 龙日升, 刘伟军 等. 基板预热温度对激光金属沉积成形零件微观组织的影响[J]. 工程设计学报, 2009, 16(3): 210~216

【14】C. Zhou, N. Wang, H. Xu. Comparison of thermal cycling behavior of plasma-sprayed nanostructured and traditional thermal barrier coatings[J]. Materials Science and Engineering: A, 2007, 452-453: 569~574

【15】W. Jiang, K. Yahiaoui, F. R. Hall. Finite element predictions of temperature distributions in a multipass welded piping branch junction[J]. Journal of Pressure Vessel Technology, 2005, 127(1): 7~12

引用该论文

Doan Tatkhoa,Li Dichen,Lu Bingheng,Zhang Anfeng,He Bin,Do Xuantuoi. Effect of Scanning Methods on the Cracking of the DZ125L Superalloy in Laser Direct Metal Forming[J]. Chinese Journal of Lasers, 2012, 39(10): 1003002

Doan Tatkhoa,李涤尘,卢秉恒,张安峰,贺斌,Do Xuantuoi. 扫描方式对激光金属直接成形DZ125L高温合金薄壁件开裂的影响[J]. 中国激光, 2012, 39(10): 1003002

被引情况

【1】Do Xuantuoi,李涤尘,张安峰,贺斌. 激光金属直接成形DZ125L高温合金柱状晶连续生长的数值模拟与实验研究. 中国激光, 2013, 40(6): 603008--1

【2】姜亚琼,林鑫,马良,谭华,杨海欧,黄卫东. 沉积路径对激光立体成形钛合金T型缘条热/应力场的影响. 中国激光, 2014, 41(7): 703003--1

【3】齐宝路,张安峰,张文龙,师博飞,李涤尘. 激光定向生长修复DZ125L柱状晶叶片力学性能研究. 中国激光, 2015, 42(6): 603002--1

【4】崔爱永,胡芳友,魏华凯,刘浩东,黄飞,王志. 航空钛合金激光3D梯度改性去应力修复研究. 中国激光, 2015, 42(s1): 103007--1

【5】贾帅,傅戈雁,方琴琴,石世宏,姜付兵. 激光光内送粉线形悬垂分支结构直接成形. 中国激光, 2016, 43(3): 303008--1

【6】王 潭,张安峰,梁少端,严深平,张连重,李涤尘. 超声振动辅助激光金属成形IN718沉积态 组织及性能的研究. 中国激光, 2016, 43(11): 1102005--1

【7】严深平,张安峰,李涤尘,曹伟产,张连重,王潭,梁少端. 粉末混合均匀性及W粉形态对激光直接成形W-Cu复合材料成形质量的影响. 中国激光, 2017, 44(6): 602001--1

【8】杨海欧,韩加军,林鑫,黄卫东. 热处理对激光立体成形DZ125高温合金组织的影响. 中国激光, 2018, 45(11): 1102004--1

【9】卞宏友,左士刚,曲伸,杨光,王伟,王维. 激光沉积成形分区环形扫描路径生成算法. 激光与光电子学进展, 2019, 56(2): 21601--1

您的浏览器不支持PDF插件,请使用最新的(Chrome/Fire Fox等)浏览器.或者您还可以点击此处下载该论文PDF