钛酸锶钡薄膜的室温光学性能研究

Optical Properties of (Ba0.75Sr0.25)TiO3 Film at Room Temperature
作者单位
西北大学 信息科学与技术学院, 陕西 西安 710127
摘要
采用溶胶-凝胶法制备了(Ba0.75Sr0.25)TiO3薄膜, 研究了不同退火温度下样品的物相结构、薄膜的光致发光性能和光学透过率。结果表明: 室温下非晶钛酸锶钡薄膜在蓝光激发下具有明显的发光现象, 发光波长范围是500~650 nm, 峰值在525 nm附近。延长非晶态薄膜的退火时间能够显著提高样品的发光强度, 且发光强度随薄膜厚度增加而增大。晶态薄膜有微弱的发光现象。透射谱测试结果表明, 钛酸锶钡薄膜在可见光范围内具有良好的光学透过率。
Abstract
(Ba0.75Sr0.25)TiO3 thin film was prepared by sol-gel process. The phase structure, photoluminescence properties and optical transmittance of the films annealed at different temperature were studied respectively. The results show that a strong photoluminescence phenomenon can be observed under blue light excited at room temperature. The emission band is from 500 nm to 650 nm, and the peak is about 525 nm. An enhanced intensity of photoluminescence property was measured by increasing the anneal time for amorphous films. Moreover, the photoluminescence intensity also increases with the film thickness. A weak photoluminescence peak was observed in crystalline film. In addition, both the crystalline and amorphous films have good optical transmittance in the visible light region.

高永进, 赵丽丽, 张智翔, 廖付友, 朱红丹. 钛酸锶钡薄膜的室温光学性能研究[J]. 发光学报, 2012, 33(10): 1074. GAO Yong-jin, ZHAO Li-li, ZHANG Zhi-xiang, LIAO Fu-you, ZHU Hong-dan. Optical Properties of (Ba0.75Sr0.25)TiO3 Film at Room Temperature[J]. Chinese Journal of Luminescence, 2012, 33(10): 1074.

关于本站 Cookie 的使用提示

中国光学期刊网使用基于 cookie 的技术来更好地为您提供各项服务,点击此处了解我们的隐私策略。 如您需继续使用本网站,请您授权我们使用本地 cookie 来保存部分信息。
全站搜索
您最值得信赖的光电行业旗舰网络服务平台!