强激光与粒子束, 2012, 24 (11): 2613, 网络出版: 2012-10-12   

湿法和溶脱法的亚微米ZnO:Al光栅制备

Farbrication of submicron ZnO:Al gratings with wet etching and lift-off technology
作者单位
同济大学 精密光学工程技术研究所, 上海 200092
摘要
以激光干涉法得到的光刻胶图案为掩模, 采用湿法刻蚀和溶脱-剥离法制备了具有良好减反射特性的亚微米掺铝氧化锌(ZnO:Al, AZO)光栅。表面形貌特征和反射光谱测试结果表明, 湿法刻蚀较溶脱-剥离法得到的AZO光栅表面更为粗糙, 两者均方根粗糙度分别为25.4, 7.6 nm。在400~900 nm波段, 两种方法制备的周期和高度相同的光栅, 平均总反射率分别由AZO薄膜的12.5%下降到8.3%和10.2%。两者的平均镜面反射率分别为6.2%和6.6%, 平均漫反射率分别为2.1%和3.6%。湿法刻蚀得到的表面较为粗糙AZO光栅的漫反射明显减弱, 从而导致总的减反特性优于溶脱-剥离法得到的表面起伏相对较小的AZO光栅。
Abstract
With a photoresist pattern acquired by laser interference lithography as an etch mask, submicron aluminum-doped zinc oxide (AZO) gratings, which had excellent anti-reflection properties, were acquired by using wet etching and lift-off technology. The surface morphology was observed by an atomic force microscopy (AFM), and the reflectance spectrum was tested with a ultra-visible spectrophotometer. Results show that the AZO grating fabricated by wet etching is rougher than that acquired by lift-off technology, and the root mean squares of surface topographies of the two gratings are 25.4 nm and 7.6 nm, respectively. In the waveband range of 400-900 nm, two structural AZO gratings with the same period (980 nm) and height (160 nm) decrease the average total reflectance from 12.5% of the AZO thin film to 8.3% and 10.2%, respectively. The average specular reflectance are 6.2% and 6.6%, and diffuse reflectance are 2.1% and 3.6%, accordingly. It is concluded that wet etching-made AZO grating with rough surfaces decrease diffuse reflectance greatly, and are better in decreasing total reflectance than lift-off-made AZO grating with flatter surfaces.

刘仁臣, 吴永刚, 夏子奂, 王振华, 唐平林, 梁钊铭. 湿法和溶脱法的亚微米ZnO:Al光栅制备[J]. 强激光与粒子束, 2012, 24(11): 2613. Liu Renchen, Wu Yonggang, Xia Zihuan, Wang Zhenhua, Tang Pinglin, Liang Zhaoming. Farbrication of submicron ZnO:Al gratings with wet etching and lift-off technology[J]. High Power Laser and Particle Beams, 2012, 24(11): 2613.

本文已被 4 篇论文引用
被引统计数据来源于中国光学期刊网
引用该论文: TXT   |   EndNote

相关论文

加载中...

关于本站 Cookie 的使用提示

中国光学期刊网使用基于 cookie 的技术来更好地为您提供各项服务,点击此处了解我们的隐私策略。 如您需继续使用本网站,请您授权我们使用本地 cookie 来保存部分信息。
全站搜索
您最值得信赖的光电行业旗舰网络服务平台!