激光技术, 2012, 36 (6): 802, 网络出版: 2012-11-07   

双磷酸氧钛钾晶体倍频特性的实验研究

Experiment research of frequency doubling characteristics in tandem double KTiOPO4 crystal
作者单位
军械工程学院 光学与电子工程系, 石家庄 050003
摘要
为了研究双块磷酸氧钛钾(KTiOPO4,KTP)晶体串接倍频对于提高绿光倍频激光器的转换效率的作用, 采用长度分别为6mm, 8mm和15mm的3块KTP晶体两两串接组合进行了实验验证, 绘制了单块晶体倍频和双块晶体串接倍频时的转换效率曲线, 并对其进行了比较分析。结果表明, 基频光功率密度从520MW/cm2到750MW/cm2时, 双块KTP晶体正交串接倍频不仅比双块KTP晶体平行串接倍频的转换效率高近10%, 而且比长度是两块晶体之和的单块长KTP晶体的倍频转换效率高近30%。这一实验结果对于提高绿光倍频激光器的转换效率有一定的意义。
Abstract
In order to study effect of two pieces of potassium titanyl phosphate (KTiOPO4, KTP) crystal in tandem to improve the conversion efficiency of the frequency doubling green lasers, three pieces of KTP crystal in 6mm, 8mm, 15mm long separately were used in experiments with two of them in tandem. The conversion efficiency curves of monolithic crystal and two tandem crystals were drawn. The results of scheme of two-piece KTP crystal orthogonal or parallel tandem were compared with that of a single monolithic KTP. The result shows that two-piece KTP orthogonal tandem has nearly 10% higher conversion efficiency than two-piece KTP parallel tandem, and two-piece KTP orthogonal tandem has nearly 30% higher conversion efficiency than a monolithic one in the same length with power density at fundamental frequency from 520MW/cm2 to 750MW/cm2. The experimental results have a certain significance in improving the conversion efficiency of frequency doubling green lasers.

兰明伟, 沈学举, 李晓明. 双磷酸氧钛钾晶体倍频特性的实验研究[J]. 激光技术, 2012, 36(6): 802. LAN Ming-wei, SHEN Xue-ju, LI Xiao-ming. Experiment research of frequency doubling characteristics in tandem double KTiOPO4 crystal[J]. Laser Technology, 2012, 36(6): 802.

本文已被 1 篇论文引用
被引统计数据来源于中国光学期刊网
引用该论文: TXT   |   EndNote

相关论文

加载中...

关于本站 Cookie 的使用提示

中国光学期刊网使用基于 cookie 的技术来更好地为您提供各项服务,点击此处了解我们的隐私策略。 如您需继续使用本网站,请您授权我们使用本地 cookie 来保存部分信息。
全站搜索
您最值得信赖的光电行业旗舰网络服务平台!