氮掺杂碳气凝胶电极材料的制备及性能

Preparation and performance of nitrogen-doped carbon aerogels as electrode materials
作者单位
1 中国工程物理研究院 激光聚变研究中心, 四川 绵阳 621900
2 西华大学 材料科学与工程学院, 成都 610039
摘要
以三聚氰胺(M)、间苯二酚(R)和甲醛(F)为原料,经溶胶-凝胶法、超临界干燥和高温碳化制备了系列的氮掺杂碳气凝胶(NCAs)。X射线光电子能谱(XPS)分析表明,氮元素成功地引入到碳气凝胶中,并且可以通过调节三聚氰胺掺杂量来控制氮掺杂量; 扫描电子显微镜(SEM)和N2吸附测试显示出不同氮掺杂量的碳气凝胶的微观结构差异较大,随着氮含量的增加,比表面积有先减后增的趋势; 在6 mol/L KOH溶液中进行的恒流充放电和循环伏安测试表明,引入氮元素能够极大地改善碳气凝胶的电化学性能,最高比电容量达176 F·g-1,并且凝胶具有良好的电容特性和可逆性。
Abstract
Nitrogen-doped carbon aerogels (NCAs) were synthesized from melamine, resorcinol and formaldehyde by sol-gel, supercritical drying and high-temperature carbonization process. The structure properties and function of the NCAs were characterized by means of XPS, SEM and nitrogen adsorption, showing that the nitrogen was successfully doped into carbon aerogels. Meanwhile, the N-doping content and the microstructures of the NCAs distinctly depend on the amount of melamine. Besides, the electrochemical performances of the NCAs were tested by galvanostatic charge-discharge and cyclic voltammetry in 6 mol/L KOH solution, and the results indicate that their electrochemical performances are greatly improved after N-doping with the highest specific capacitance reaching 176 F·g-1.

刘西川, 袁磊, 冯灏, 付志兵, 王朝阳, 孙卫国, 唐永建. 氮掺杂碳气凝胶电极材料的制备及性能[J]. 强激光与粒子束, 2012, 24(12): 2848. Liu Xichuan, Yuan Lei, Feng Hao, Fu Zhibing, Wang Chaoyang, Sun Weiguo, Tang Yongjian. Preparation and performance of nitrogen-doped carbon aerogels as electrode materials[J]. High Power Laser and Particle Beams, 2012, 24(12): 2848.

本文已被 1 篇论文引用
被引统计数据来源于中国光学期刊网
引用该论文: TXT   |   EndNote

相关论文

加载中...

关于本站 Cookie 的使用提示

中国光学期刊网使用基于 cookie 的技术来更好地为您提供各项服务,点击此处了解我们的隐私策略。 如您需继续使用本网站,请您授权我们使用本地 cookie 来保存部分信息。
全站搜索
您最值得信赖的光电行业旗舰网络服务平台!