激光技术, 2013, 37 (2): 270, 网络出版: 2013-03-27   

激光冲击波作用下3003H16铝合金板料层裂的研究

Research of spalling on 3003H16 aluminium alloy sheet under laser shock wave
作者单位
江苏大学 机械工程学院, 镇江 212013
摘要
为了得到工艺参量对层裂的影响, 运用有限元模拟的方法, 采用最大拉应力瞬时断裂准则来判断板料是否发生层裂, 并对各参量对层裂的影响进行了分析; 进行了激光冲击成形试验, 用电子扫描显微镜对冲击后的试样进行观察, 并运用应力波传播分析了层裂的产生、发展、形成。结果表明, 层裂易发生在激光冲击区域内, 其次是在光斑边缘处, 而在冲击区域外不可能发生层裂; 脉冲宽度、峰值压力和板料厚度对层裂发生的位置影响较大, 而光斑直径对层裂发生的位置几乎没有影响。这对激光冲击成形的发展具有指导意义。
Abstract
In order to understand the influence of the technological parameters on spalling, it was analyzed by means of the finite element simulation. The maximum tensile stress instantaneous fracture criterion was used to check spalling happened or not. Then, the experiment of laser shock forming was carried out. The shocked samples were surveyed with a scanning electron microscope. The emerging, developing and forming of the spalling were analyzed. The results show that the spalling is susceptible to the shock region, and then the spot edge. Spalling will never happen outside the shock region. The influence of pulse width, peak pressure and sheet thickness affect the position of spalling significantly. However, the spot diameter affects it little. These have guiding significance to the development of the laser shock forming.

黄利伟, 龙昆, 黄宇, 郭海平, 丰琅, 周俊, 马睿佳. 激光冲击波作用下3003H16铝合金板料层裂的研究[J]. 激光技术, 2013, 37(2): 270. HUANG Li-wei, LONG Kun, HUANG Yu, GUO Hai-ping, FENG Lang, ZHON Jun, MA Rui-jia. Research of spalling on 3003H16 aluminium alloy sheet under laser shock wave[J]. Laser Technology, 2013, 37(2): 270.

本文已被 1 篇论文引用
被引统计数据来源于中国光学期刊网
引用该论文: TXT   |   EndNote

相关论文

加载中...

关于本站 Cookie 的使用提示

中国光学期刊网使用基于 cookie 的技术来更好地为您提供各项服务,点击此处了解我们的隐私策略。 如您需继续使用本网站,请您授权我们使用本地 cookie 来保存部分信息。
全站搜索
您最值得信赖的光电行业旗舰网络服务平台!