LaLu0.7Er0.3O3纳米多晶的制备、结构和光谱特性

Preparation, structural and spectral properties of LaLu0.7Er0.3O3 polycrystalline

  • 摘要
  • 论文信息
  • 参考文献
  • 被引情况
  • PDF全文
分享:

摘要

采用共沉淀法制备了LaLu0.7 Er0.3 O3 的纳米多晶粉体。对它进行了X射线粉末衍射测试, 根据衍射峰宽估算了粉体颗粒的尺寸,同时利用Rietveld全谱拟合方法确定了它的结构。在室温下, 测试研究了它的吸收和光致发光谱。并利用380 nm光激发,测试了1.5 μm红外 (4II15/2 ) 光的荧光衰减情况, 给出了相应荧光寿命。结果表明,LaLu1-x Erx O3 是一种值得深入研究并具有潜在应用价值 的红外激光材料。

Abstract

LaLu0.7 Er0.3 O3 polycrystalline was synthesized by the co-precipitation method. It’s structure were determined by Rietveld refinement to X-ray powder diffraction, and the size of powder particles was also estimated. Its absorption and photoluminescence spectra at room temperature were measured. Under the excitation of 380 nm light, the 1.5 μm decay curve of Er3 + (4II15/2 ) was also measured, and the decay time was given. It’s shown that LaLu1-x Erx O3 is a potential infrared laser material, which has application value.

Newport宣传-MKS新实验室计划
补充资料

中图分类号:O782

DOI:10.3969/j.issn.1007-5461.2013.02.006

所属栏目:激光技术与器件

基金项目:国家自然科学基金(90922003, 51172236, 50872135)、中科院知识创新(YYYJ-1002)资助项目

收稿日期:2012-03-28

修改稿日期:2012-04-13

网络出版日期:--

作者单位    点击查看

周鹏宇:中国科学院安徽光学精密机械研究所安徽省光子器件与材料重点实验室,安徽 合肥 230031中国科学院研究生院,北京 100049
张庆礼:中国科学院安徽光学精密机械研究所安徽省光子器件与材料重点实验室,安徽 合肥 230031
宁凯杰:中国科学院安徽光学精密机械研究所安徽省光子器件与材料重点实验室,安徽 合肥 230031中国科学院研究生院,北京 100049
杨华军:中国科学院安徽光学精密机械研究所安徽省光子器件与材料重点实验室,安徽 合肥 230031中国科学院研究生院,北京 100049
孙敦陆:中国科学院安徽光学精密机械研究所安徽省光子器件与材料重点实验室,安徽 合肥 230031
罗建乔:中国科学院安徽光学精密机械研究所安徽省光子器件与材料重点实验室,安徽 合肥 230031
殷绍唐:中国科学院安徽光学精密机械研究所安徽省光子器件与材料重点实验室,安徽 合肥 230031

联系人作者:周鹏宇(neozpy@mail.ustc.edu.cn)

备注:周鹏宇 (1986-), 辽宁人,研究生,从事新型光电功能材料研究。

【1】Konz F, Frenz M, Romano V, et al. Active and passive Q-switching of a 2.79 μm Er-Cr-YSGG laser [J]. Opt. Commun., 1993, 103(5-6): 398-404.

【2】Tempus M, Luthy W, Weber H P, et al. 2.79 μm YSGG: CrEr laser-pumped at 790 nm [J]. IEEE J. Quantum Electron., 1994, 30(11): 2608-2611.

【3】Hogele A, Horbe G, Lubatschowski H, et al. 2.70 μm Cr, Er: YSGG laser with high output energy and FTIR-Q-switch [J]. Opt. Commun., 1996, 125(1-3): 90-94.

【4】Kintz G J, Allen R, Esterowitz L. CW and pulsed 2.8 μm laser-emission from diode-pumped Er3 + -LiYF4 at room-temperature [J]. Appl. Phys. Lett., 1987, 50(22): 1553-1555.

【5】Xu Jun, Su Liangbi, Xu Xiaodong, et al. Recent developments and research frontier of laser crystals [J]. J. Inorg. Mater. (无机材料学报), 2006, 21(5): 1025-1030 (in Chinese).

【6】Li Xiuzhi, Lin Zhoubin, Zhang Lizhen, et al. Growth, thermal and spectroscopic characterization of Er3 + :NaY(MoO4 )2 crystal [J]. J. Cryst. Growth, 2006, 293(1): 157-161.

【7】Ito K, Tezuka K, Hinatsu Y. Preparation, magnetic susceptibility, and specific heat on interlanthanide perovskites ABO3 (A=La-Nd, B=Dy-Lu) [J]. Journal of Solid State Chemistry, 2001, 156: 173-179.

【8】Shao Shufang, Zhang Qingli, Sun Dunlu, et al. Study on raw material preparation and structure of LD-pumped Nd:GGG laser crystal [J]. Chinese Journal of Quantum Electronics (量子电子学报), 2005, 22(4): 565-569 (in Chinese).

【9】Zhang Lide, Mou Jimei. Nanomaterials and Nanostructures (纳米材料和纳米结构) [M]. Beijing: Science Press, 2001: 146-153, 227-232 (in Chinese).

【10】Larson A C, Von Dreele R B. General Structure Analysis System (GSAS) [R]. Los Alamos National Laboratory Report LAUR, 2004, 86-748.

【11】Zhang Busheng. Solution and evolution to the nonisotropic temperature factor for crystal [J]. Journal of Hebei Normal University (Natural Science) (河北师范大学学报(自然科学版)), 1997, 21(2): 149-152 (in Chinese).

【12】Lu Yanling, Wang Jun, Sun Baode. Research progress of 2 μm waveband laser crystals [J]. Journal of Inorganic Materials (无机材料学报), 2005, 20(3): 514-521 (in Chinese).

引用该论文

ZHOU Peng-yu,ZHANG Qing-li,NING Kai-jie,YANG Hua-jun,SUN Dun-lu,LUO Jian-qiao,YIN Shao-tang. Preparation, structural and spectral properties of LaLu0.7Er0.3O3 polycrystalline[J]. Chinese Journal of Quantum Electronics, 2013, 30(2): 162-168

周鹏宇,张庆礼,宁凯杰,杨华军,孙敦陆,罗建乔,殷绍唐. LaLu0.7Er0.3O3纳米多晶的制备、结构和光谱特性[J]. 量子电子学报, 2013, 30(2): 162-168

被引情况

【1】陈晓波,李崧,胡丽丽,耿珠峰,赵国营,王科志,陶京富,林伟,杨国建,郭平. Er3+(10%):碲酸盐玻璃的近红外量子剪裁发光. 量子电子学报, 2017, 34(3): 257-263

【2】代雨航,李剑,张莹,朱忠丽. Er,Yb∶(LaLu)2O3透明陶瓷制备及上转换发光性能. 发光学报, 2018, 39(4): 488-493

您的浏览器不支持PDF插件,请使用最新的(Chrome/Fire Fox等)浏览器.或者您还可以点击此处下载该论文PDF