光子学报, 2013, 42 (5): 526, 网络出版: 2013-05-22   

Yb/P/Al共掺双包层光纤的制备与激光性能

Fabrication and Laser Performance of Yb/P/Al Codoped Doubleclad Fibers
作者单位
1 富通集团有限公司,浙江 富阳 311422
2 浙江大学 光电信息工程学系 现代光学仪器国家重点实验室,杭州 310027
摘要
采用改进化学汽相沉积结合溶液掺杂法制备了Yb/P/Al共掺的石英光纤预制棒,通过光纤芯层的组份和制备工艺的优化,实现了Yb3+的高浓度掺杂和均匀掺杂.预制棒芯层Yb2O3掺杂浓度达到~4wt.%,Yb3+在1 080 nm处荧光寿命为1 780 μs.成功拉制出内包层截面形状为八边形的双包层光纤,纤芯直径为7.5 μm,包层吸收系数达到~5 dB/m@976 nm.利用拉制的掺镱双包层光纤开展了全光纤结构的掺镱光纤激光器性能测试实验,实现了5.15 W的激光输出,斜率效率达到76%.
Abstract
Yb/P/Al codoped silica glass preforms are fabricated by MCVD process combined with the solution doping technique. Highly and homogeneously doping of Yb3+ is realized by optimization of the core composition and fabrication process. The Yb2O3 concentration in preform core is up to ~4 wt.% and Yb3+ fluorescence lifetime at 1080nm reaches 1 780 μs. Doubleclad fibers with octagonal inner cladding are successfully drawn from the preform, the fiber core diameter is 7.5 μm and the clad absorption coefficicent is up to ~5 dB/m@976 nm. The operation of the cladding pumped allfiber laser is demonstrated using Ybdoped doubleclad fibers. Fiber lasers with output power of 5.15 W and slope efficiency of 76% are obtained.

冯高锋, 杨军勇, 卢卫民, 葛锡良, 刘伟, 陈滔, 姜培培, 沈永行. Yb/P/Al共掺双包层光纤的制备与激光性能[J]. 光子学报, 2013, 42(5): 526. FENG Gaofeng, YANG Junyong, LU Weimin, GE Xiliang, LIU Wei, CHEN Tao, JIANG Peipei, SHEN Yonghang. Fabrication and Laser Performance of Yb/P/Al Codoped Doubleclad Fibers[J]. ACTA PHOTONICA SINICA, 2013, 42(5): 526.

本文已被 1 篇论文引用
被引统计数据来源于中国光学期刊网
引用该论文: TXT   |   EndNote

相关论文

加载中...

关于本站 Cookie 的使用提示

中国光学期刊网使用基于 cookie 的技术来更好地为您提供各项服务,点击此处了解我们的隐私策略。 如您需继续使用本网站,请您授权我们使用本地 cookie 来保存部分信息。
全站搜索
您最值得信赖的光电行业旗舰网络服务平台!