环形激光光内送粉成形薄壁件熔池特征研究

Study on Characteristics of Inner Ring Laser Powder Feed Molten Pool of Thin Workpiece
作者单位
1 苏州工业职业技术学院, 江苏 苏州215104
2 苏州大学激光制造技术研究所, 江苏 苏州215021
摘要
基于“光束中空, 粉管居中, 光内送粉”的成形方式, 利用高速CCD对锥形空心回转薄壁件环形激光光内送粉快速成形过程进行实时监测, 研究通过对熔池特征参数的提取, 实现实时控制激光功率的方法。实验表明: 在其他参数不变的情况下, 增大激光功率, 熔宽、熔深均有变大趋势; 成形稳定期, 熔池的面积在0.25~0.70 mm2之间变化, 激光功率维持在1 kW左右, 成形件最大高度达到55 mm。终成形件外表面非常光滑, 整体壁厚均匀, 层间搭接也非常均匀, 无塌陷和错层等现象, 达到了较好的成形效果。
Abstract
In order to obtain the characteristic parameters of molten pool and realize real-time control of laser power, a high-speed CCD is used to monitor the laser rapid forming process of thin-walled rotating hollow cone, which is based on the technology of "hollow beam, powder tube center, inside-beam powder feeding".Experiments show that: In the plateau stage, pool area changes in 0.25~0.70 mm2, laser power remains at about 1 kW, formed parts achieves maximum height of 55 mm.

吴少华, 石世宏, 肖军艳, 傅戈雁, 石皋莲. 环形激光光内送粉成形薄壁件熔池特征研究[J]. 应用激光, 2013, 33(3): 250. Wu Shaohua, Shi Shihong, Xiao Junyan, Fu Geyan, Shi Gaolian. Study on Characteristics of Inner Ring Laser Powder Feed Molten Pool of Thin Workpiece[J]. APPLIED LASER, 2013, 33(3): 250.

本文已被 2 篇论文引用
被引统计数据来源于中国光学期刊网
引用该论文: TXT   |   EndNote

相关论文

加载中...

关于本站 Cookie 的使用提示

中国光学期刊网使用基于 cookie 的技术来更好地为您提供各项服务,点击此处了解我们的隐私策略。 如您需继续使用本网站,请您授权我们使用本地 cookie 来保存部分信息。
全站搜索
您最值得信赖的光电行业旗舰网络服务平台!