PC/YAG∶Ce荧光树脂的制备及光谱分析

Preparation and Luminescent Properties of PC/YAG∶Ce Fluorescent Resin
作者单位
1 华南师范大学光电子材料与技术研究所 微纳米光子功能材料与器件重点实验室, 广东 广州510631
2 广东工业技术研究院, 广东 广州510650
摘要
采用熔融共混法和高温压模法制备出PC/YAG∶Ce荧光树脂片, 样品经减薄和抛光处理后, 通过X射线衍射仪(XRD)、扫描电子显微镜(SEM)、光致发光(PL)、透射光谱等测试手段进行分析。厚度为0.87 mm的样品在500~800 nm范围内的透过率约为65%。样品主相为Y3Al5O12, 在342 nm和448 nm有两个激发峰。样品的发射光谱在532 nm有一宽峰, 属于Ce3+的5d→4f特征跃迁发射。荧光树脂片中荧光粉含量越高, 样品发射强度越大, 是一种适合用于白光LED封装的新型荧光材料。
Abstract
PC/YAG∶Ce fluorescent resin pieces were prepared by using the methods of compound-melting and high-temperature molding. The transmittance of the YAG∶Ce/PC fluorescent resin in 500~800 nm reaches approximately 65% (0.87 mm thick, double sides polished). The fluorescent resin was characterized by XRD, SEM and PL. The X-ray diffraction (XRD) patterns indicate that the fluorescent resin was pure Y3Al5O12 phase. The scanning electron microscopy (SEM) images show that YAG phosphor is distributed evenly in the fluorescent resin. The excitation spectra had a weak peak at 342 nm and a strong band at 448 nm. The broad emission peaks at about 532 nm can be attributed to 5d→4f transition of Ce3+ ions. The higher the content of fluorescent powder is, the stronger the luminesence intensity of the samples will be. All results show that YAG∶Ce/PC fluorescent resin may be a promising fluorescent material for white LEDs.

肖瑶, 范广涵, 皮辉, 许毅钦, 郑树文, 陈志武, 贺龙飞, 张力, 张涛. PC/YAG∶Ce荧光树脂的制备及光谱分析[J]. 发光学报, 2013, 34(11): 1419. XIAO Yao, FAN Guang-han, PI Hui, XU Yi-qin, ZHENG Shu-wen, CHENG Zhi-wu, HE Long-fei, ZHANG Li, ZHANG Tao. Preparation and Luminescent Properties of PC/YAG∶Ce Fluorescent Resin[J]. Chinese Journal of Luminescence, 2013, 34(11): 1419.

本文已被 2 篇论文引用
被引统计数据来源于中国光学期刊网
引用该论文: TXT   |   EndNote

相关论文

加载中...

关于本站 Cookie 的使用提示

中国光学期刊网使用基于 cookie 的技术来更好地为您提供各项服务,点击此处了解我们的隐私策略。 如您需继续使用本网站,请您授权我们使用本地 cookie 来保存部分信息。
全站搜索
您最值得信赖的光电行业旗舰网络服务平台!