应用激光, 2013, 33 (4): 398, 网络出版: 2013-12-04   

45号钢光纤激光表面熔凝处理工艺研究

Research on Fiber Laser Remelting of 45 Steel
作者单位
1 中国钢研科技集团有限公司 新冶高科技集团有限公司, 北京 100081
2 中国钢研科技集团有限公司, 北京 100081
摘要
利用光纤激光对45号钢进行了激光熔凝强化处理, 研究了激光功率对单道和多道激光熔凝层深度的影响, 并分析了熔凝层组织、显微硬度和耐磨性能。结果表明, 单道激光熔凝硬化层组织主要为马氏体, 硬度可达HV 750, 深度达到1.0 mm以上。多道激光熔凝硬化层平均硬度约HV 450, 硬化层显微硬度呈周期性变化, 后道激光处理对前道硬化层存在回火软化作用。激光强化处理后的试样相比于未处理试样, 抗磨损性能提高了约50%。
Abstract
45 steel was remelted by fiber laser in this study. The effect of laser power on the remelted layer depth was investigated based on single pass processing and multi-passes processing. The microstructure, microhardness and wear resistance of the harden layer were also analyzed. The result indicates that the martensite is the dominating microsturcture in the remelted layer, and the microhardness reaches 750 HV for single pass processing. The depth of remelted layer is more than 1 mm. On the other hand , the average microhardness is about 450 HV after multi-passes processing. The microhardness distribution of the remelted layer changes periodically owing to temper softning effect by the later laser pass. Compared with the untreated samples of 45 steel, the wear resistance increases about 50% by the fiber laser remelted.

屈岳波, 赵琳, 张瑞华, 张岩, 裴悦凯, 田志凌. 45号钢光纤激光表面熔凝处理工艺研究[J]. 应用激光, 2013, 33(4): 398. Qu Yuebo, Zhao Lin, Zhang Ruihua, Zhang Yan, Pei Yuekai, Tian Zhiling. Research on Fiber Laser Remelting of 45 Steel[J]. APPLIED LASER, 2013, 33(4): 398.

本文已被 1 篇论文引用
被引统计数据来源于中国光学期刊网
引用该论文: TXT   |   EndNote

相关论文

加载中...

关于本站 Cookie 的使用提示

中国光学期刊网使用基于 cookie 的技术来更好地为您提供各项服务,点击此处了解我们的隐私策略。 如您需继续使用本网站,请您授权我们使用本地 cookie 来保存部分信息。
全站搜索
您最值得信赖的光电行业旗舰网络服务平台!