发光学报, 2013, 34 (12): 1646, 网络出版: 2013-12-20   

Al组分对MOCVD制备的AlxGa1-xN/AlN/GaN HEMT电学和结构性质的影响

Influence of Al Composition on Electrical and Structural Properties of AlxGa1-xN/AlN/GaN HEMT Materials Grown by MOCVD
作者单位
1 北京工业大学电子信息与控制工程学院 光电子技术省部共建教育部重点实验室, 北京100124
2 中国科学院苏州纳米技术与纳米仿生研究所 纳米器件与应用重点实验室, 江苏 苏州215123
摘要
采用金属有机化合物化学气相沉积(MOCVD)方法制备了不同Al组分(x=0.19,0.22,0.25,0.32)的AlxGa1-xN/AlN/GaN 结构的高电子迁移率晶体管(HEMT)材料。研究了AlxGa1-xN势垒层中Al组分对HEMT材料电学性质和结构性质的影响。研究结果表明,在一定的Al组分范围内,二维电子气(2DEG)浓度和迁移率随着Al组分的升高而增大。然而,过高的Al组分导致HEMT材料表面粗糙度增大,2DEG迁移率降低,该实验现象在另一方面得到了原子力显微镜测试结果的验证。在最佳Al组分(25%)范围内,获得的HEMT材料的2DEG浓度和室温迁移率分别达到1.2×1013 cm-2和1 680 cm2/(V·s),方块电阻低至310 Ω/□。
Abstract
AlxGa1-xN/AlN/GaN high electron mobility transistor (HEMT) materials with different Al compositions (x=0.19, 0.22, 0.25, 0.32) were grown on sapphire substrates by metalorganic chemical vapor deposition (MOCVD). The effects of Al composition on electrical and structural properties of HEMTs materials were analyzed. It is observed that two-dimensional electron gas (2DEG) density and mobility are improved with the raising of Al content within a certain range. However, too high Al composition will make the surface turn to be rougher and the mobility deteriorate, which was reinforced by the test results of atomic force microscopy (AFM). The optimum Al content is 25%. Based on this, the HEMT materials showed a high 2DEG density of 1.2×1013 cm-2 with a low sheet resistance of 310 Ω/□, and highly Hall mobility of 1 680 cm2/(V·s) at room temperature.

陈翔, 邢艳辉, 韩军, 霍文娟, 钟林健, 崔明, 范亚明, 朱建军, 张宝顺. Al组分对MOCVD制备的AlxGa1-xN/AlN/GaN HEMT电学和结构性质的影响[J]. 发光学报, 2013, 34(12): 1646. CHEN Xiang, XING Yan-hui, HAN Jun, HUO Wen-juan, ZHONG Lin-jian, CUI Ming, FAN Ya-ming, ZHU Jian-jun, ZHANG Bao-shun. Influence of Al Composition on Electrical and Structural Properties of AlxGa1-xN/AlN/GaN HEMT Materials Grown by MOCVD[J]. Chinese Journal of Luminescence, 2013, 34(12): 1646.

本文已被 2 篇论文引用
被引统计数据来源于中国光学期刊网
引用该论文: TXT   |   EndNote

相关论文

加载中...

关于本站 Cookie 的使用提示

中国光学期刊网使用基于 cookie 的技术来更好地为您提供各项服务,点击此处了解我们的隐私策略。 如您需继续使用本网站,请您授权我们使用本地 cookie 来保存部分信息。
全站搜索
您最值得信赖的光电行业旗舰网络服务平台!