发光学报, 2014, 35 (3): 317, 网络出版: 2014-03-11
Sr3B2O6∶Eu3+,Li+荧光粉的合成与发光性能
Synthesis and Luminescent Properties of Sr3B2O6∶Eu3+,Li+ Phosphor
摘要
采用高温固相法合成Sr3B2O6∶Eu3+,Li+红色荧光粉, 考察了激活剂Eu3+和电荷补偿剂Li+浓度对Sr3B2O6∶Eu3+,Li+荧光粉发光性能的影响。结果表明: 适量掺杂Eu3+、Li+离子并不改变Sr3B2O6的结构。当Eu3+掺杂量为4%、Li+的掺杂量为8%时, 在900 ℃下灼烧2 h可以得到发光性能最佳的Sr2.9B2O6∶0.04Eu3+,0.08Li+红色荧光粉。以394 nm的近紫外光激发时, Sr3B2O6∶Eu3+, Li+荧光粉发射出红光, 对应于Eu3+的4f-4f 跃迁, 其中以614 nm附近的5D0→7F2跃迁发光最强, 是一种有潜力用于白光LED的红色荧光粉。
Abstract
The red phosphor Sr3B2O6∶Eu3+,Li+ was prepared by high temperature solid-state method. The effects of the concentration of activating agent Eu3+and sensitizing agent Li+ on luminescent properties of Sr3B2O6∶Eu3+,Li+ were investigated. The results show that there is not obvious structure transformation of Sr3B2O6 after appropriate amounts of Eu3+ and Li+ doping. The optimal doping content of Eu3+ and Li+ are 4% and 8%, respectively. The optimal temperature is 900 ℃ for 2 h. The phosphor Sr3B2O6∶Eu3+,Li+ can be excited by 394 nm near-UV light and emits red light corresponding to the 4f-4f transition of Eu3+. Its strongest emission peak is attributed to the 5D0→7F2 transition of Eu3+ at about 614 nm. The phosphor could be a promising red phosphor for white LED.
杨英, 陈永杰, 肖林久, 耿秀娟, 谢颖, 闵广全. Sr3B2O6∶Eu3+,Li+荧光粉的合成与发光性能[J]. 发光学报, 2014, 35(3): 317. YANG Ying, CHEN Yong-jie, XIAO Lin-jiu, GENG Xiu-juan, XIE Ying, MIN Guang-quan. Synthesis and Luminescent Properties of Sr3B2O6∶Eu3+,Li+ Phosphor[J]. Chinese Journal of Luminescence, 2014, 35(3): 317.