2.9微米Tm,Ho:LuAG激光晶体的生长与光谱性能研究

Growth and Spectroscopic Properties of the 2.9 μm Tm,Ho:LuAG Laser Crystal

  • 摘要
  • 论文信息
  • 参考文献
  • 被引情况
  • PDF全文
分享:

摘要

采用提拉法成功生长出了高光学质量的Tm,Ho:LuAG(Lu3Al5O12)激光晶体,对其光谱性能进行了研究。测量了晶体320~3000 nm范围内的吸收光谱,在784 nm附近有较宽的吸收带,半峰全宽约为12 nm。用784 nm半导体激光器(LD)作激发源,测量了晶体2800~3000 nm范围内的稳态荧光光谱,并用光参量振荡(OPO)脉冲激光激发,测量了晶体的瞬态荧光光谱,对数据曲线进行指数衰减拟合,获得了晶体2.9 μm附近波长激光上下能级5I6和5I7的寿命,分别为51 μs和7.5 ms。与Tm,HoYAG(Y3Al5O12)晶体的光谱参数进行了比较,结果表明,Tm,Ho:LuAG是一种相对容易获得2.911 μm中红外激光输出的激光晶体。

Abstract

Tm,Ho:LuAG crystal with high optical quality is grown successfully by the Czochralski method, and its spectroscopic characteristics are investigated. The absorption spectrum of Tm,Ho:LuAG crystal in the range of 320~3000 nm is measured, and a wide absorption band with full width at half maximum (FWHM) of 12 nm is located near 784 nm. The fluorescence spectrum in the range of 2800~3000 nm is measured by exciting with 784 nm laser diode (LD). The fluorescence decay curves are also measured by exciting with optical parameter oscillation (OPO) laser. The lifetimes of the upper lever 5I6 (51 μs) and lower lever 5I7 (7.5 ms) are obtained by fitting the exponential decay curves. Compared with the parameters of Tm,HoYAG (Y3Al5O12) crystal, it suggests that Tm,Ho:LuAG crystal is a potential mid-infrared laser material to realize the laser at 2.911 μm.

Newport宣传-MKS新实验室计划
补充资料

中图分类号:O734+.3

DOI:10.3788/aos201434.0416006

所属栏目:材料

基金项目:国家自然科学基金(91122021,51272254,61205173,51172236,50932005)

收稿日期:2013-11-06

修改稿日期:2013-11-28

网络出版日期:--

作者单位    点击查看

张会丽:中国科学院安徽光学精密机械研究所安徽省光子器件与材料重点实验室, 安徽 合肥 230031中国科学院大学, 北京 100049
孙敦陆:中国科学院安徽光学精密机械研究所安徽省光子器件与材料重点实验室, 安徽 合肥 230031
罗建乔:中国科学院安徽光学精密机械研究所安徽省光子器件与材料重点实验室, 安徽 合肥 230031
陈家康:中国科学院安徽光学精密机械研究所安徽省光子器件与材料重点实验室, 安徽 合肥 230031中国科学院大学, 北京 100049
曹世豪:中国科学院安徽光学精密机械研究所安徽省光子器件与材料重点实验室, 安徽 合肥 230031中国科学院大学, 北京 100049
程毛杰:中国科学院安徽光学精密机械研究所安徽省光子器件与材料重点实验室, 安徽 合肥 230031
张庆礼:中国科学院安徽光学精密机械研究所安徽省光子器件与材料重点实验室, 安徽 合肥 230031
殷绍唐:中国科学院安徽光学精密机械研究所安徽省光子器件与材料重点实验室, 安徽 合肥 230031

联系人作者:张会丽(zhanghuili269@163.com)

备注:张会丽(1989—),女,硕士,主要从事激光晶体生长及性能方面的研究。

【1】K L Vodopyanov, F Ganikhanov, J P Maffetone, et al.. ZnGeP2 optical parametric oscillator with 3.8~12.4 μm tenability [J]. Opt Lett, 2000, 25(11): 841-843.

【2】Chen Jiakang, Sun Dunlu, Zhang Huili, et al.. Research progress of 2.7~3 μm rare earth laser crystals [J]. J Synth Cryst, 2013, 42(5): 824-832.
陈家康, 孙敦陆, 张会丽, 等. 2.7~3 μm稀土激光晶体研究进展 [J]. 人工晶体学报, 2013, 42(5): 824-832.

【3】Yang Jingwei, Wang Li, Wu Xianyou, et al.. Numerical simulation and experimental study on thermal effects of 2.94 μm Er:YAG laser [J]. Acta Optica Sinica, 2012, 32(6): 0614002.
杨经纬, 王礼, 吴先友, 等. 2.94 μm Er:YAG激光热效应数值模拟及实验研究 [J]. 光学学报, 2012, 32(6): 0614002.

【4】Chen Jiakang, Sun Dunlu, Luo Jianqiao, et al.. Spectroscopic properties and diode end-pumped 2.79 μm laser performance of Er,PrGYSGG crystal [J]. Opt Express, 2013, 21(20): 23425-23432.

【5】Wang Li, Yang Jingwei, Wu Xianyou, et al.. 2.79 μm high peak power and narrow pulse electro-optically Q-switched Cr,ErYSGG laser [J]. Chinese J Lasers, 2013, 40(1): 0106002.
王礼, 杨经纬, 吴先友, 等. 2.79 μm窄脉冲、高峰值功率电光调Q-Cr,ErYSGG激光器 [J]. 中国激光, 2013, 40(1): 0106002.

【6】W S Rabinovich, S R Bowman, B J Feldman, et al.. Tunable laser pumped 3 μm HoYA1O3 laser [J]. IEEE J Quantum Electron, 1991, 27(4): 895-897.

【7】A F Umyskov, Y D Zavartsev, A I Zagumennyi, et al.. Efficient 3-μm Cr3+,Yb3+,Ho3+:YSGG crystal laser [J]. Quantum Lett, 1996, 26(9): 771-772.

【8】Pan Zhonghan, Wu Lusheng, Lu Shiping, et al.. An optical parametric oscillator (OPO) tunable laser in 1.47~4 μm [J]. Acta Optica Sinica, 1885, 5(7): 590-593.
潘忠汉, 吴路生, 鲁士平, 等. 1.47~4 μm光参量振荡器 [J]. 光学学报, 1985, 5(7): 590-593.

【9】D D Hudson, R J Williams, M J Withford, et al.. Single-frequency fiber laser operating at 2.9 μm [J]. Opt Lett, 2013, 38(14): 2388-2390.

【10】Wang Xiaodan, Xu Xiaodong, Zang Taocheng, et al.. Growth and spectral properties of TmLu3Al5O12 crystal [J]. J Chin Rare Earth Soc, 2009, 27(6): 745-749.
王晓丹, 徐晓东, 臧涛成, 等. TmLu3Al5O12晶体的生长光谱性能研究 [J]. 中国稀土学报, 2009, 27(6): 745-749.

【11】M V Derdzyan, K L Ovanesyan, A G Petrosyan, et al.. Radiation hardness of LuAGCe and LuAGPr scintillator crystals [J]. J Cryst Growth, 2012, 361: 212-216.

【12】K Beil, S T Fredrich-Thornton, F Tellkamp, et al.. Thermal and laser properties of YbLuAG for kW thin disk lasers [J]. Opt Express, 2010, 18(20): 20712-20722.

【13】Wang Xiaodan, Xu Xiaodong, Wang Jingya, et al.. Spectrum and laser properties of Nd:Lu3Al5O12 crystal [J]. Chinese J Lasers, 2012, 39(5): 0506001.
王晓丹, 徐晓东, 王静雅, 等. Nd:Lu3Al5O12晶体光谱与激光性能研究 [J]. 中国激光, 2012, 39(5): 0506001.

【14】N P Barnes, E D Filer, F L Naranjo, et al.. Spectroscopic and lasing properties of HoTmLuAG [J]. Opt Lett, 1993, 18(9): 708-710.

【15】K Scholle, E Heuman, G Huber. Single mode Tm and Tm,Ho:LuAG laser for lidar applications [J]. Laser Phys Lett, 2004, 1(6): 285-290.

【16】V Kushawaha, Y Chen, Y Yan, et al.. High-efficiency continuous-wave diode-pumped TmHoLuAG at 2.1 μm [J]. Appl Phys B, 1996, 62(1): 109-111.

【17】Y Kuwano, K Suda, N Ishizawa, et al.. Crystal growth and properties of (Lu,Y)3Al5O12[J]. J Cryst Growth, 2004, 260(1-2): 159-165.

【18】A A Kamenski. Laser Crystal [M]. Beijing: Science Press, 1981. 66-67.
卡明斯基. 激光晶体 [M]. 北京: 科学出版社,1981. 66-67.

【19】A Diening, S Kück. Spectroscopy and diode-pumped laser oscillation of Yb3+, Ho3+-doped yttrium scandium gallium garnet [J]. J Appl Phys, 2000, 87(9): 4063-4068.

引用该论文

Zhang Huili,Sun Dunlu,Luo Jianqiao,Chen Jiakang,Cao Shihao,Cheng Maojie,Zhang Qingli,Yin Shaotang. Growth and Spectroscopic Properties of the 2.9 μm Tm,Ho:LuAG Laser Crystal[J]. Acta Optica Sinica, 2014, 34(4): 0416006

张会丽,孙敦陆,罗建乔,陈家康,曹世豪,程毛杰,张庆礼,殷绍唐. 2.9微米Tm,Ho:LuAG激光晶体的生长与光谱性能研究[J]. 光学学报, 2014, 34(4): 0416006

您的浏览器不支持PDF插件,请使用最新的(Chrome/Fire Fox等)浏览器.或者您还可以点击此处下载该论文PDF