溶胶凝胶法制备Ti1-xFexO2纳米颗粒及磁性能研究

Preparation and Magnetic Properties of Ti1-xFexO2 Nanoparticles by Sol-Gel Process
作者单位
吉林师范大学物理学院, 吉林 四平 136000
摘要
采用溶胶凝胶法制备了稀磁半导体Ti1-xFexO2(x=0~0.050) 的纳米颗粒, 在氩气氛围中以500℃对样品进行退火处理,并通过差热/热重综合热分析仪(TG-DTA)、X射线衍射仪(XRD)、拉曼光谱(Raman)分析了纳米颗粒的结构和相变温度。使用振动样品磁场计(VSM)测试了样品的磁性能。研究发现: 经500℃氩气氛围下退火处理后, 样品均为锐钛矿结构, 并且随掺杂量增加晶粒尺寸减小。VSM测试结果表明, 样品在中心区域均出现明显的磁滞现象。
Abstract
Ti1-xFexO2(x=0~0.050)diluted magnetic semiconductor nanoparticles were prepared by sol-gel method, and were annealed in Ar under 500℃. The crystal structure and the phase transition temperature of the nanoparticles were analyzed by thermogravimetry-differential thermal analysis (TG-DTA), X-ray diffraction (XRD) patterns and Raman spectroscopy. The magnetic properties of the nanoparticles were measured by vibrating sample magnetometer (VSM). The crystal structure of the Fe doped TiO2 sample is found to be anatase after annealing at 500℃. The grain size of the samples decreases with the increase of the Fe content. The magnetic properties of the samples show the obvious hysteresis in the central areas.

刘立华, 王璐, 张勇, 华中, 董丽荣, 徐帅. 溶胶凝胶法制备Ti1-xFexO2纳米颗粒及磁性能研究[J]. 光散射学报, 2011, 23(1): 42. LIU Li-hua, WANG Lu, ZHANG Yong, HUA Zhong, DONG Li-rong, XU Shuai. Preparation and Magnetic Properties of Ti1-xFexO2 Nanoparticles by Sol-Gel Process[J]. The Journal of Light Scattering, 2011, 23(1): 42.

关于本站 Cookie 的使用提示

中国光学期刊网使用基于 cookie 的技术来更好地为您提供各项服务,点击此处了解我们的隐私策略。 如您需继续使用本网站,请您授权我们使用本地 cookie 来保存部分信息。
全站搜索
您最值得信赖的光电行业旗舰网络服务平台!