发光学报, 2014, 35 (4): 404, 网络出版: 2014-05-08  

Ag/ZnO纳米结构的荧光增强效应

Photoluminescence Enhancement from Ag/ZnO Nanostructures
作者单位
1 浙江工业大学之江学院 理学系, 浙江 杭州310024
2 浙江大学物理系 硅材料国家重点实验室, 浙江 杭州310027
摘要
利用化学合成方法制备了Ag纳米线和ZnO量子点。对这两种纳米结构的表面形貌、晶体结构和光学性质分别进行了研究。结果表明: Ag纳米线和ZnO量子点均为单晶结构, 平均直径分别为160 nm和5 nm左右。将Ag纳米线混入ZnO量子点可以使其紫外荧光显著增强, 其中位于345 nm和383 nm 的荧光分别增强30倍和12倍。这与Ag纳米线和ZnO量子点混合体系的局域表面等离子体共振耦合吸收峰位相一致, 说明该体系存在两种共振耦合模式。该研究结果为将来开发ZnO基纳米发光器件提供了一条新的途径。
Abstract
Ag nanowires and ZnO quantum dots were fabricated by chemical methods. The surface morphologies, structures and optical properties were investigated. It is found that both Ag nanowires and ZnO quantum dots exhibit single crystal structure with average diameters of 160 nm and 5 nm, respectively. The enhanced ultraviolet photoluminscence was observed from ZnO quantum dots after mixed with Ag nanowires. The enhancement ratio is 30-fold for emission at 345 nm and 12-fold for that at 383 nm. These enhancement emission positions coincide with the localized surface plasmon resonant absorption peaks of Ag nanowires, which indicate that there are two localized surface plasmon resonant modes in Ag nanowires. This work may give a new approach to design ZnO based nano light-emitting devices.

徐天宁, 李佳, 李翔, 隋成华, 吴惠桢. Ag/ZnO纳米结构的荧光增强效应[J]. 发光学报, 2014, 35(4): 404. XU Tian-ning, LI Jia, LI Xiang, SUI Cheng-hua, WU Hui-zhen. Photoluminescence Enhancement from Ag/ZnO Nanostructures[J]. Chinese Journal of Luminescence, 2014, 35(4): 404.

关于本站 Cookie 的使用提示

中国光学期刊网使用基于 cookie 的技术来更好地为您提供各项服务,点击此处了解我们的隐私策略。 如您需继续使用本网站,请您授权我们使用本地 cookie 来保存部分信息。
全站搜索
您最值得信赖的光电行业旗舰网络服务平台!