不同粒径YAG荧光粉对LED封装光源的影响研究

Influence Research on LED Encapsulation Light Source from YAG Phosphor with Different Particle Size
作者单位
上海应用技术学院与理学院, 上海 201418
摘要
挑选国内某知名荧光粉企业的三种YAG荧光粉作为研究对象, 三种样品的激发光谱相同, 中心粒径(D50)分别为9.3、13.6、16.7 μm, 用这三种荧光粉, 在相同粉胶质量比, 相同点胶量的情况下, 使用3014型号支架, 制作出白光LED灯珠样品。使用分光分度计分别测量老化前后样品的各项光学参数。试验结果显示: 随着荧光粉中心粒径的增大, 色温向着高色温方向移动; 当色温相同时, 随着中心粒径的增大, 光通量随之增大, 使用100 mA电流加速老化一个星期情况下, 随着荧光粉粒径的增大, 光衰逐渐减小。
Abstract
Three kinds of YAG phosphor is chosen from a famous phosphor enterprise in China as research objects. The samples have same laser spectrum and central particle sizes (D50) are 9.3 μm, 13.6 μm and 16.7 μm respectively. At the condition of same filler-asphalt mass ratio and bonding volume, with the phosphor and 3014 type stand, white light LED lamp bead samples are produced. Optical parameters of the samples before and after aging are measured respectively by a spectrophotometer. Test results show that with the increasing of the center particle size of phosphor, color temperature approaches to the direction of high color temperature. When color temperature is constant, with the increasing of center particle size, luminous flux increases. Luminous decay reduces gradually with the increasing of phosphor particle size at the condition of one week accelerating aging time and 100 mA current.

张生冬, 王凤超, 邹军. 不同粒径YAG荧光粉对LED封装光源的影响研究[J]. 光电技术应用, 2014, 29(4): 21. ZHANG Sheng-dong, WANG Feng-chao, ZOU Jun. Influence Research on LED Encapsulation Light Source from YAG Phosphor with Different Particle Size[J]. Electro-Optic Technology Application, 2014, 29(4): 21.

本文已被 5 篇论文引用
被引统计数据来源于中国光学期刊网
引用该论文: TXT   |   EndNote

相关论文

加载中...

关于本站 Cookie 的使用提示

中国光学期刊网使用基于 cookie 的技术来更好地为您提供各项服务,点击此处了解我们的隐私策略。 如您需继续使用本网站,请您授权我们使用本地 cookie 来保存部分信息。
全站搜索
您最值得信赖的光电行业旗舰网络服务平台!