激光与光电子学进展, 2014, 51 (12): 121602, 网络出版: 2014-12-02   

高温导致三结太阳电池电致发光谱变化 下载: 636次

Change of Electroluminescence Spectra of Solar Cells Caused by Heating
作者单位
中国工程物理研究院流体物理研究所, 四川 绵阳 621900
摘要
高温下半导体材料性能会发生变化,影响太阳电池光电转换效率。为了了解GaInP/GaAs/Ge 三结太阳电池在聚光和高温条件下的工作性质,研究了热加载后的三结太阳电池样品在定压下的电致发光谱,发现受热后GaInP 顶电池和GaAs 中电池的电致发光谱的强度发生变化,出现峰值反转的现象。结合光照下伏-安特性、暗伏安特性及外量子效率分析了这种现象产生的原因,即加热过程在GaInP 顶电池中引入晶格结构缺陷,导致其电致发光强度变弱,同时顶电池并联电阻变小,GaAs 中电池分压有所增加,发光增强,整个样品的电致发光谱出现峰值反转现象。结果表明GaAs 中电池比GaInP 顶电池具有更好的耐热性。
Abstract
The photoelectric characteristics of solar cells can be changed after heated, which ultimately influence the converting efficiency of solar cell. Electroluminescence spectra of GaInP/GaAs/Ge triple junction solar cell under constant voltage are investigated in order to understand the working properties of such cells under concentration and heating condition. It is found that the luminescence peaks of GaInP top cell and GaAs middle cell change and reverse after the solar cells are heated. By considering the current-voltage characteristic and external quantum efficiency, the origin of this phenomenon is found to attribute to the introduction of deep level defects in the crystal. GaAs middle cell is found to be more tolerant to heat-induced damage than GaInP top cell.

任攀, 吴凌远, 王伟平, 刘国栋. 高温导致三结太阳电池电致发光谱变化[J]. 激光与光电子学进展, 2014, 51(12): 121602. Ren Pan, Wu Lingyuan, Wang Weiping, Liu Guodong. Change of Electroluminescence Spectra of Solar Cells Caused by Heating[J]. Laser & Optoelectronics Progress, 2014, 51(12): 121602.

本文已被 1 篇论文引用
被引统计数据来源于中国光学期刊网