SiO2包覆对ZnS纳米材料发光的增强机制

Mechanism of the enhanced fluorescence of SiO2-coated ZnS nanoparticles
作者单位
长春理工大学 理学院, 吉林 长春 130022
摘要
为了明确团聚现象及表面性质对ZnS纳米材料发光性质的影响, 采用SiO2对ZnS材料进行了表面修饰, 并对ZnS及ZnS/SiO2复合材料的光学性质进行对比研究。采用吸收光谱分析了包覆前后光吸收性质的差异, 发现SiO2包覆后ZnS纳米材料的带边由333 nm红移至360 nm。为了研究ZnS纳米材料与ZnS/SiO2纳米复合材料的光发射性质, 分别对含纳米材料的水溶液样品及粉末样品的发光光谱进行了采集。对比研究的结果表明, SiO2包覆后ZnS纳米材料在蓝紫光区的发光得到了明显增强。以氙灯作为激发光源所获得荧光光谱显示ZnS/SiO2粉末样品发光的积分强度增大为原来的17.5倍, 但相同条件下针对溶液样品的测试结果显示其发光强度只增大了1.1倍, 这种增强可用SiO2的存在抑制了ZnS纳米粒子间的团聚来解释, 且这一推断由325 nm紫外激光激发下获得的光致发光数据进行了验证。
Abstract
In order to investigate the influence of aggregation and surface effect on the optical properties of ZnS nanoparticles, SiO2 is used to modify the surface of ZnS nanoparticles. The optical properties of the synthesized ZnS and ZnS/SiO2 nanoparticles are both studied for making a comparison. According to the absorption spectra recorded by an ultraviolet-visible spectrophotometer, the band gap edge red-shifts from 333 nm to 360 nm. To analyze the emission properties, the fluorescence spectra of the solution and the powders containing the ZnS or ZnS/SiO2 nanoparticles are both collected. It is found that the light emission of the ZnS nanoparticles in the violet to blue region is enhanced obviously when SiO2 is introduced. When the samples are excitated by a xenon lamp, the integrated fluorescence intensity of the ZnS/SiO2 nanoparticles is enhanced by 17.5 times. However, a much smaller enhancement is found in the measurement for the solution samples. The fluorescence is only 1.1 times higher after coating ZnS nanoparticles by SiO2. The inhibition of the aggregation between the ZnS nanoparticles by the SiO2 coated layer is supposed to be responsible for the enhancement, which is confirmed by the photoluminescence data where a 325 nm He-Cd laser is used as the excitation source.

赵健, 楚学影, 李金华, 方铉, 王晓华. SiO2包覆对ZnS纳米材料发光的增强机制[J]. 中国光学, 2014, 7(6): 925. ZHAO Jian, CHU Xue-ying, LI Jin-hua, FANG Xuan, WANG Xiao-hua. Mechanism of the enhanced fluorescence of SiO2-coated ZnS nanoparticles[J]. Chinese Optics, 2014, 7(6): 925.

本文已被 1 篇论文引用
被引统计数据来源于中国光学期刊网
引用该论文: TXT   |   EndNote

相关论文

加载中...

关于本站 Cookie 的使用提示

中国光学期刊网使用基于 cookie 的技术来更好地为您提供各项服务,点击此处了解我们的隐私策略。 如您需继续使用本网站,请您授权我们使用本地 cookie 来保存部分信息。
全站搜索
您最值得信赖的光电行业旗舰网络服务平台!