1064nm纳秒激光对石墨烯的损伤效应研究

1064nm nanosecond laser induced damage effect on graphene
作者单位
中国工程物理研究院 流体物理研究所, 四川 绵阳 621900
摘要
通过化学气相沉积法制备,并转移到基片得到1~3层石墨烯样品.利用霍尔效应及微区拉曼光谱测量,结合光学显微镜观察,分析了不同层数石墨烯在1064 nm纳秒激光辐照下的损伤特性.实验发现1~3层石墨烯的激光损伤阈值依次降低,分别为:单层0.45 J/cm2,2层0.34 J/cm2,3层0.23 J/cm2.激光强度超过阈值时,石墨烯薄膜电阻增大,载流子迁移率降低.通过光学显微镜观察发现局部区域破损,破损区域的拉曼光谱中1580 cm-1左右的G峰和2700 cm-1左右的2D峰高度比发生变化.实验结果表明1064 nm纳秒激光辐照石墨烯主要为剥离作用.
Abstract
The mono-bi-and trilayer graphene samples were prepared by chemical vapor deposition method and transferred to substrate.Damage effect of the graphene under 1064 nm nanosecond laser irradiation was quantified by taking Hall Effect and Raman spectra measurements.The results show that,the laser induced damage threshold values of the mono-bi-and trilayer graphene samples decrease accordingly:mono layer,0.45 J/cm2;bilayer,0.34 J/cm2;3 layer,0.23 J/cm2.When the laser energy is higher than the threshold,the sheet resistance of graphene increases,and the carrier mobility decreases.Damaged area was observed by optical microscope after high energy laser irradiation.In the damaged area,the Raman intensity ratios of the G peak (1580 cm-1) to the 2D peak (2700 cm-1) decrease.The results demonstrate that the 1064 nm nanosecond laser irradiation can exfoliate the multilayer graphene without inducing structure defects.

吴凌远, 李阳龙, 刘国栋, 王伟平. 1064nm纳秒激光对石墨烯的损伤效应研究[J]. 强激光与粒子束, 2015, 27(8): 081009. Wu Lingyuan, Li Yanglong, Liu Guodong, Wang Weiping. 1064nm nanosecond laser induced damage effect on graphene[J]. High Power Laser and Particle Beams, 2015, 27(8): 081009.

关于本站 Cookie 的使用提示

中国光学期刊网使用基于 cookie 的技术来更好地为您提供各项服务,点击此处了解我们的隐私策略。 如您需继续使用本网站,请您授权我们使用本地 cookie 来保存部分信息。
全站搜索
您最值得信赖的光电行业旗舰网络服务平台!