激光技术, 2015, 39 (5): 594, 网络出版: 2015-09-10   

光内同轴送粉立面堆积成形实验研究

Experimental study about vertical surface accumulation with coaxial inside-beam power feeding
作者单位
苏州大学 机电工程学院, 苏州 215021
摘要
为了得到表面粗糙度低的立面变径回转体,采用中空激光光内同轴送粉技术进行立面堆积的方法,着重对中空激光立面堆积的优点以及激光光头姿态、光头提升量Δz、激光功率对立面堆积成形件表面粗糙度的影响进行了理论分析和实验验证.在立面堆积过程中,激光光头始终保持与熔道表面垂直,同时对提升量Δz、激光功率进行实时控制,最终得到表面光滑的立面回转体成形件,其粗糙度Ra为0.497μm~2.163μm;Rz为1.992μm~7.447μm.结果表明,该方法在立面堆积方面具有适用性,可以得到表面粗糙度低的成型件.
Abstract
In order to obtain a rotator with low surface roughness and variable radii,based on the technology of laser cladding manufacturing process with coaxial inside-beam powder feeding,the advantages of coaxial inside-beam power feeding accumulation and the influence of the posture,increment in z axis (Δz) and laser power of the laser head on the surface roughness were analyzed theoretically and verified experimentally.In the accumulation process,laser head was kept perpendicular to the molten surface,Δz and laser power were effectively controlled.Finally,a fine rotator was obtained with low roughness,i.e.,Ra=0.497μm~2.163μm;Rz=1.992μm~7.447μm.Experimental results show that this method is applicable for laser accumulation on vertical surfaces and the molding parts have lower roughness.

孟伟栋, 石世宏, 傅戈雁, 王涛, 杨轼, 史建军. 光内同轴送粉立面堆积成形实验研究[J]. 激光技术, 2015, 39(5): 594. MENG Weidong, SHI Shihong, FU Geyan, WANG Tao, YANG Shi, SHI Janjun. Experimental study about vertical surface accumulation with coaxial inside-beam power feeding[J]. Laser Technology, 2015, 39(5): 594.

本文已被 5 篇论文引用
被引统计数据来源于中国光学期刊网
引用该论文: TXT   |   EndNote

相关论文

加载中...

关于本站 Cookie 的使用提示

中国光学期刊网使用基于 cookie 的技术来更好地为您提供各项服务,点击此处了解我们的隐私策略。 如您需继续使用本网站,请您授权我们使用本地 cookie 来保存部分信息。
全站搜索
您最值得信赖的光电行业旗舰网络服务平台!